Corrosion resistance of CrN and CrCN/CrN coatings deposited using cathodic arc evaporation in Ringer's and Hank's solutions

被引：70
|
作者：
Gilewicz, A. [1 ]
Chmielewska, P. [1 ]
Murzynski, D. [1 ]
Dobruchowska, E. [1 ]
Warcholinski, B. [1 ]
机构：
[1] Koszalin Univ Technol, Fac Technol & Educ, Koszalin, Poland
来源：
SURFACE & COATINGS TECHNOLOGY | 2016年 / 299卷
关键词：
Corrosion; CrN; CrCN/CrN; Tafel curves; Ringer's solution; Hank's solution; CR/CRN MULTILAYER COATINGS; COATED STAINLESS-STEEL; CHROMIUM NITRIDE; HARD COATINGS; TRIBOLOGICAL PROPERTIES; BILAYER PERIOD; BEHAVIOR; GROWTH; WEAR;
D O I：
10.1016/j.surfcoat.2016.04.069
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This paper presents the corrosion resistance of CrN monolayer coatings and CrCN/CrN multilayer coatings deposited by cathodic arc evaporation onto X39Cr13 stainless steel. Corrosion tests of the coating-substrate systems were conducted in Ringer's and Hank's solutions, usually used as infusion liquids. The parameters such as corrosion potential, corrosion current density and polarisation resistance were determined on the basis of the potentiodynamic polarisation curves. The corrosion properties of coatings in as-deposited state and after the polishing were compared. The results show that coated substrates are characterised by under half the corrosion potential and 10-times lower corrosion current density compared to the reference substrate (without coating). The corrosion parameters for polished coatings are slightly worse than unpolished, which is related to the method of coating deposition. The amount and distribution of macroparticles on the surface of the tested coatings are also presented. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码：7 / 14
页数：8
相关论文
共 50 条
  • [31] The effect of Cr/Zr chemical composition ratios on the mechanical properties of CrN/ZrN multilayered coatings deposited by cathodic arc deposition system
    Chen, Siao-Fan
    Kuo, Yu-Chu
    Wang, Chaur-Jeng
    Huang, Sung-Hsiu
    Lee, Jyh-Wei
    Chan, Yu-Chen
    Chen, Hsien-Wei
    Duh, Jenq-Gong
    Hsieh, Tsung-Eong
    SURFACE & COATINGS TECHNOLOGY, 2013, 231 : 247 - 252
  • [32] Wear and corrosion resistance of CrN/TiN superlattice coatings deposited by a combined deep oscillation magnetron sputtering and pulsed dc magnetron sputtering
    Ou, Y. X.
    Lin, J.
    Tong, S.
    Che, H. L.
    Sproul, W. D.
    Lei, M. K.
    APPLIED SURFACE SCIENCE, 2015, 351 : 332 - 343
  • [33] Wear resistance and solid lubricity of molybdenum-containing nitride coatings deposited by cathodic arc evaporation
    Yang, Qi
    SURFACE & COATINGS TECHNOLOGY, 2017, 332 : 283 - 295
  • [34] A comparative study of the corrosion and ion release behaviour of chromium oxide coatings exposed to saline, Ringer's and Hank's physiological solutions
    Oje, A. M.
    Ogwu, A. A.
    Oje, Alex I.
    Tsendzughul, Nathaniel
    Rahman, S. Ur
    CORROSION SCIENCE, 2020, 167
  • [35] A new approach to improve SCC resistance of austenitic stainless steel with a thin CrN film, deposited by cathodic vacuum arc deposition technique
    Tillmann, W.
    Vogli, E.
    Mohapatra, S.
    SURFACE & COATINGS TECHNOLOGY, 2007, 202 (4-7) : 750 - 754
  • [36] EFFECT OF ARC CURRENT ON MECHANICAL PROPERTIES OF AlCrN COATINGS DEPOSITED USING CATHODIC ARC EVAPORATION
    Warcholinski, B.
    Gilewicz, A.
    Kuprin, A. S.
    PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2022, (04): : 141 - 146
  • [37] Comparative Investigation and Characterization of the Scratch and Wear Resistance Behavior of TiN, CrN, AlTiN and AlCrN Cathodic Arc PVD Coatings
    Akeem Yusuf Adesina
    Zuhair M. Gasem
    Abdul Samad Mohammed
    Arabian Journal for Science and Engineering, 2019, 44 : 10355 - 10371
  • [38] Mechanical properties of Mo(C)N coatings deposited using cathodic arc evaporation
    Warcholinski, B.
    Gilewicz, A.
    Kuznetsova, T. A.
    Zubar, T. I.
    Chizhik, S. A.
    Abetkovskaia, S. O.
    Lapitskaya, V. A.
    SURFACE & COATINGS TECHNOLOGY, 2017, 319 : 117 - 128
  • [39] Effect of Silicon Concentration on the Properties of Al-Cr-Si-N Coatings Deposited Using Cathodic Arc Evaporation
    Warcholinski, Bogdan
    Gilewicz, Adam
    Myslinski, Piotr
    Dobruchowska, Ewa
    Murzynski, Dawid
    Kuznetsova, Tatyana A.
    MATERIALS, 2020, 13 (21) : 1 - 22
  • [40] Al-Mn based coatings deposited by cathodic arc evaporation for corrosion protection of AISI 4140 alloy steel
    Dobruchowska, E.
    Gilewicz, A.
    Warcholinski, B.
    Libralesso, L.
    Batory, D.
    Szparaga, L.
    Murzynski, D.
    Ratajski, J.
    SURFACE & COATINGS TECHNOLOGY, 2019, 362 : 345 - 354
12345