The effect of chloride on cement mortar subjected to sulfate exposure at low temperature

The effect of chloride on the performance of cement mortars made with CEMI and CEMI blended with 10% limestone filler and subjected to sulfate attack was investigated. The specimens were exposed to the combined action of chloride (0%, 0.5%, 1.0% and 2% of CI-) and sulfate (0.6% SO42-) for 630 days at 5 +/- 0.5 degrees C. The performance of the mortar cubes was assessed by means of visual inspection and loss of mass. The mineralogy of the deterioration products was determined by infra-red spectroscopy and Xray diffraction, and scanning electron microscopy was used to examine the microstructure of the specimens. Chemical analysis of the test solutions was also carried out at 540 days of immersion in order to assess the end concentrations of calcium, sulfate and magnesium ions. All the specimens suffered from the thaumasite form of sulfate attack, except those stored in the combined sulfate and 2.0% chloride solution, which showed better performance within the 630-day study. The greatest deterioration occurred in mortars made with CEMI blended with 10% limestone filler. Based on visual and mass assessments, it was found that the effect of chloride on thaumasite degradation depended on chloride concentration, accelerating the damage at 0.5% and mitigating it at 2% in the conditions investigated. This is probably related to the reduction in calcite solubility and the increase in Friedel's salt deposition observed as the chloride level increased in solution. (C) 2014 Elsevier Ltd. All rights reserved.