Spray pyrolysis of MgO templates on Hastelloy C276 and 310-austenitic stainless steel substrates for YBa2Cu3O7 (YBCO) deposition by pulsed laser deposition

被引：18
作者：
Al Khateeb, Shadi [1 ]
Button, T. W. [1 ]
Abell, J. S. [1 ]
机构：
[1] Univ Birmingham, Sch Met & Mat, Birmingham B15 2TT, W Midlands, England
来源：
SUPERCONDUCTOR SCIENCE & TECHNOLOGY | 2010年 / 23卷 / 09期
关键词：
O THIN-FILMS; BUFFER LAYERS; TEXTURED NI; COATED CONDUCTORS; INTERGRANULAR CORROSION; EPITAXIAL-GROWTH; METAL; TAPES; EVAPORATION; ORIENTATION;
D O I：
10.1088/0953-2048/23/9/095001
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
MgO thin films were deposited on Hastelloy C276 (HC) and 310 austenitic stainless steel by the spray pyrolysis technique, using magnesium nitrate and magnesium acetate as precursors. Thermogravimetrical analysis of the decomposition of the precursors was used to provide a guideline temperature for the thin film deposition. It was suggested that an amorphous MgO thin film was deposited on both 310-stainless steel and Hastelloy C-276 when using low concentration of the magnesium nitrate precursor. Higher concentrations were needed to obtain (200) oriented MgO films on C276. However, 310-stainless steel was found to not be a suitable substrate for MgO thin film deposition due to surface instability. A (200) oriented MgO thin film was grown on Hastelloy C276 using a magnesium acetate precursor at a much lower concentration compared to the nitrate precursor. The characterization of the thin films was done using scanning electron microscopy, x-ray photoelectron spectroscopy, atomic force microscopy, x-ray diffraction 2 theta-scans, rocking curves (omega-scans), and pole figure measurements. MgO was found to have a very weak in-plane texture.
引用
收藏
页数：9
相关论文
共 71 条
[1]  
*AM SOC MET, 2003, ASM HDB CORR FUND TE
[2]  
*AM SOC MET, 1991, ASM INT HDB COMM HEA
[3]  
*ASM INT, 1980, MET HDB ASM INT, V3
[4]   Inclined-substrate deposition of biaxially textured template for coated conductors [J].
Balachandran, U ;
Ma, B ;
Li, A ;
Fisher, BL ;
Koritala, RE ;
Erck, RA ;
Dorris, SE .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2002, 378 (PART 2) :950-954
[5]  
Balachandran UB, 2004, AIP CONF PROC, V711, P637, DOI 10.1063/1.1774624
[6]  
BALACHANDRAN UB, 2004, ADV CRYOGENIC ENG A, V50, P637
[7]   Thin MgO layers for effective hopping transport of electrons [J].
Balkenende, AR ;
Bogaerts, AAMB ;
Scholtz, JJ ;
Tijburg, RRM ;
Willems, HX .
PHILIPS JOURNAL OF RESEARCH, 1996, 50 (3-4) :365-373
[8]   HIGH JC Y-BA-CU-O THIN-FILMS PREPARED BY A SPRAY PYROLYSIS METHOD [J].
BAN, E ;
MATSUOKA, Y ;
OGAWA, H ;
KUROSAWA, K .
JOURNAL OF ALLOYS AND COMPOUNDS, 1992, 187 (01) :193-205
[9]   Nickel base substrate tapes for coated superconductor applications [J].
Bhattacharjee, Pinaki P. ;
Ray, Ranjit Kumar ;
Upadhyaya, Anish .
JOURNAL OF MATERIALS SCIENCE, 2007, 42 (06) :1984-2001
[10]   Preparation of high quality MgO thin films by ultrasonic spray pyrolysis [J].
Bian, JM ;
Li, XM ;
Chen, TL ;
Gao, XD ;
Yu, WD .
APPLIED SURFACE SCIENCE, 2004, 228 (1-4) :297-301
12345678