Investigation of optimum nucleation temperature and heating rate of cordierite glass-ceramics

被引:2
作者
Karimi, Yousef [1 ]
Zakeri, Mohammad [1 ]
Rahimipour, Mohammad Reza [1 ]
Faeghinia, Aida [1 ]
机构
[1] Mat & Energy Res Ctr, Dept Ceram, Karaj, Iran
关键词
Cordierite glasses; Glass-ceramic; Nucleation; Crystallization; CRYSTALLIZATION BEHAVIOR; TIO2; MICROSTRUCTURE;
D O I
10.3139/146.111168
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
In this survey, cordierite glass-ceramic was prepared by melting in a platinum crucible at 1580 degrees C. The effects of temperature and heating rate were studied on the nucleation and crystallization. Nucleation and crystallization temperatures were obtained by differential thermal analysis, scanning electron microscopy and X-ray diffraction. The results showed that the optimum nucleation and crystallization occurred at 810 and 1150 degrees C, respectively. According to the X-ray diffraction patterns, cordierite, rutile, quartz and MgTi2O5 phases were obtained in the crystallized glass-ceramics. The maximum bending strength of 178 MPa was obtained after the chemical strengthening of the crystallized glass ceramic.
引用
收藏
页码:184 / 187
页数:4
相关论文
共 50 条
[41]   Crystallization of cordierite-based glass-ceramics adding with Fe2O3-TiO2 [J].
Wang, Shu-ming ;
Liang, Kai-ming ;
Mei, Le-fu ;
Zhou, Feng .
HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 :1856-+
[42]   Optical investigation of Eu3+:PbF2 ceramics and transparent glass-ceramics [J].
Bensalem, C. ;
Mortier, M. ;
Vivien, D. ;
Diaf, M. .
OPTICAL MATERIALS, 2011, 33 (06) :791-798
[43]   On the variation of the maximum crystal nucleation rate temperature with glass transition temperature [J].
Gupta, Prabhat K. ;
Cassar, Daniel R. ;
Zanotto, Edgar D. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2016, 442 :34-39
[44]   Crystallization and Infrared Radiation Properties of Zn2+ Substituted α-Cordierite Based Glass-Ceramics [J].
Wang Shuming ;
Yan Qingzhi ;
Ge Changchun ;
Qi Longhao .
RARE METAL MATERIALS AND ENGINEERING, 2011, 40 :315-317
[45]   Crystallization behavior and infrared radiation property of nickel-magnesium cordierite based glass-ceramics [J].
Wang, Shuming ;
Liang, Kaiming .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2008, 354 (14) :1522-1525
[46]   Nucleation and growth of needle-like fluorapatite crystals in bioactive glass-ceramics [J].
Liu, Yong ;
Xiang, Qijun ;
Tan, Yanni ;
Sheng, Xiaoxian .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2008, 354 (10-11) :938-944
[47]   Synthesis and Characterization of Single-Phase α-Cordierite Glass-Ceramics for LTCC Substrates from Tuff [J].
Yu, Yongsheng ;
Wang, Jinghan ;
Yu, Yuanyuan ;
Yan, Zhaoli ;
Du, Yanyan ;
Chu, Pengfei ;
Jing, Qiangshan ;
Liu, Peng .
MATERIALS, 2022, 15 (24)
[48]   Glass-ceramics prepared from desulfurized electrolytic manganese residue and the nucleation promotion effect of calcium fluoride in glass phase transition [J].
Wen, Quan ;
Liu, Bo ;
Zhang, Junjie ;
Shen, Hanlin ;
Deng, Jixin ;
Zhang, Shengen .
CERAMICS INTERNATIONAL, 2024, 50 (03) :4563-4572
[49]   Synthesise and Characterization of Cordierite and Wollastonite Glass-Ceramics Derived from Industrial Wastes and Natural Raw Materials [J].
Khater, Gamal A. ;
El-Kheshen, Amany A. ;
Farag, Mohammad M. .
MATERIALS, 2022, 15 (10)
[50]   Preparation, aging behavior and interface bonding of cordierite glass-ceramics as veneer porcelain for Si3N4 ceramics [J].
Wang, Tong ;
Jiang, Lei ;
Hou, Shoujun ;
Yin, Shuang ;
Luo, Tao ;
Fang, Xia ;
Yuan, Jun ;
Tang, Xuehua ;
Wang, Yang ;
Li, Quan ;
Yang, Jian .
CERAMICS INTERNATIONAL, 2023, 49 (17) :27892-27903