High Temperature Oxidation Behavior of Yttrium Dioxide Coated Fe-20Cr Alloy

被引：9

作者：

Pillis, Marina Fuser ^{[1
]}

Correa, Olandir Vercino ^{[1
]}

Ramanathan, Lalgudi Venkataraman ^{[1
]}

机构：

[1] IPEN, Ctr Mat Sci & Technol, Av Prof Lineu Prestes 2242, BR-05508000 Sao Paulo, SP, Brazil

来源：

MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS | 2016年 / 19卷 / 03期

关键词：

Iron-chromium alloy; Yttrium dioxide; Coating; Oxidation behavior; High temperature; GRAIN-BOUNDARY SEGREGATION; FERRITIC STAINLESS-STEEL; ION-IMPLANTATION; CHROMIA SCALES; OXIDE; COATINGS; RESISTANCE; CR; INTERCONNECT; CORROSION;

D O I：

10.1590/1980-5373-MR-2015-0393

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Long term isothermal and cyclic oxidation behavior of yttrium dioxide (Y2O3) coated Fe-20Cr alloy was studied. Oxidation tests were carried out in air for periods of up to 200 hours at 1000 degrees C and the oxidation behavior of the alloy was evaluated gravimetrically. The Y2O3 coating reduced markedly the mass gain of the alloy. Energy dispersive spectroscopic analysis of scale sections on oxidized Y2O3 coated specimens revealed a Cr rich layer close to the metal/oxide interface and the presence of Y and Cr near the oxide/air interface, indicating diffusion of Cr through the Y2O3 layer. Further evidence of this diffusion was seen as change in colour of the Y2O3 coating from white to green after prolonged oxidation. X-ray diffraction analysis of the scale revealed perovskite-type YCrO3. This study attributes the increased oxidation resistance of the Y2O3 coated Fe-20Cr alloy to increased oxygen ion diffusion through the Cr2O3 scale due to YCrO3 formation and grain boundary segregated Y ion blocking alloy cation diffusion.

引用

页码：611 / 617

页数：7

共 37 条

[1] Rare earth application for heat-resisting alloys [J].

Amano, Tadaaki .

JOURNAL OF RARE EARTHS, 2010, 28 :12-21

[2]

Birks N., 1983, INTRO HIGH TEMPERATU

[3]

Chevalier S, 2002, ACTA MATER, V50, P3105, DOI 10.1016/S1359-6454(02)00106-4

[4] THE INFLUENCE OF GRAIN-BOUNDARY SEGREGATION OF Y IN CR2O3 ON THE OXIDATION OF CR METAL .2. EFFECTS OF TEMPERATURE AND DOPANT CONCENTRATION [J].

COTELL, CM ;

YUREK, GJ ;

HUSSEY, RJ ;

MITCHELL, DF ;

GRAHAM, MJ .

OXIDATION OF METALS, 1990, 34 (3-4) :201-216

[5] Study of the initial stages of oxidation of yttrium-implanted chromium using X-ray diffraction and absorption spectroscopy [J].

Cristobal, MJ ;

Gibson, PN ;

Stroosnijder, MF .

CORROSION SCIENCE, 1996, 38 (06) :805-822

[6]

Diaz LMF, 2009, DEFECT DIFFUS FORUM, V283-286, P425, DOI 10.4028/www.scientific.net/DDF.283-286.425

[7] THE INFLUENCE OF SUPERFICIALLY APPLIED OXIDE POWDERS ON THE HIGH-TEMPERATURE OXIDATION BEHAVIOR OF CR2O3-FORMING ALLOYS [J].

ECER, GM ;

SINGH, RB ;

MEIER, GH .

OXIDATION OF METALS, 1982, 18 (1-2) :55-81

[8] High temperature oxidation behaviour of yttria ( Y2O3) coated low alloy steel [J].

Ghosh, D. ;

Mukherjee, S. ;

Das, S. .

SURFACE ENGINEERING, 2014, 30 (07) :524-528

[9] Effect of LaCrO3 coating on high temperature oxidation of type 316 stainless steel [J].

Guo Pingyi ;

Zeng Chaoliu ;

Shao Yong .

JOURNAL OF RARE EARTHS, 2011, 29 (07) :698-701

[10] Computer simulation of the reactive element effect in NiO grain boundaries [J].

Harris, DJ ;

Harding, JH ;

Watson, GW .

ACTA MATERIALIA, 2000, 48 (12) :3039-3048

← 1 2 3 4 →