Effects of resin pre-coating on interfacial bond strength and toughness of laminar CFRP with and without short aramid fibre toughening

The brittle adhesive layer in carbon fiber-reinforced polymer (CFRP) laminates was strengthened by using short aramid fibers in this study. To ensure the feasibility and effectiveness of short aramid fiber interfacial toughening at the interface between the carbon-fiber face sheets, the self-prepared short aramid fibre tissue and the wettability treatment technology with resin pre-coating were applied to enable short aramid fibres to be well embedded in the uneven regions in the CFRP fabrics with fibres oriented at 0 degrees and 90 degrees to form a strong pulling resistance. The ultimate load and the mode I interlaminar fracture toughness have been improved by 75% and 103.9% from the double cantilever beam mode I crack propagation tests, respectively. The reinforcing mechanisms within the "composite adhesive layer" as a result of short aramid fibres are discussed together with detailed scanning electron microscopy observations and comparison test results.