Wear Behavior of Laser-Cladded Co-Cr-Mo Coating on γ-TiAl Substrate

被引：17

作者：

Barekat, Masoud ^{[1
]}

Razavi, Reza Shoja ^{[1
]}

Ghasemi, Ali ^{[1
]}

机构：

[1] Malek Ashtar Univ Technol, Dept Mat Engn, Shahin Shahr, Isfahan, Iran

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2017年 / 26卷 / 07期

关键词：

Co-Cr-Mo coatings; laser cladding; TiAl alloy; wear; GAMMA/CR7C3/TIC COMPOSITE COATINGS; HIGH-TEMPERATURE WEAR; INTERMETALLIC ALLOY; STRUCTURAL TRANSFORMATION; TRIBOLOGICAL BEHAVIOR; OXIDATION RESISTANCE; MICROSTRUCTURE; STELLITE-21; FRICTION; YTTRIUM;

D O I：

10.1007/s11665-017-2745-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this study, laser cladding of Co-Cr-Mo alloy on a gamma-TiAl substrate was performed to investigate the wear behavior of coated and uncoated TiAl alloy at room temperature. Dry sliding wear tests were conducted for coated and uncoated counterfaces against three pins of alumina, Inconel 718 and Co-Cr-Mo. Overall, laser cladding of Co-Cr-Mo powder resulted in the formation of a thick coating with minimal imperfections, as well as increasing the wear resistance of TiAl alloy. The results of wear tests indicated that the relative wear resistance was about 1.97, 2.17, and 1.92 for sliding against alumina, Inconel 718, and Co-Cr-Mo pins, respectively. The investigation of worn surfaces also showed that the abrasive wear mechanism was dominant for all samples. In addition, severe abrasive wear was changed to mild abrasive wear by local formation of chromium-based oxides.

引用

页码：3226 / 3238

页数：13

共 31 条

[1]

[Anonymous], 1992, TRIBOLOGY FRICTION W

[2] On the wear behavior of surface clad layers under high temperature [J].

Aoh, JN ;

Jeng, YR ;

Chu, EL ;

Wu, LT .

WEAR, 1999, 225 :1114-1122

[3]

Appel F, 2011, GAMMA TITANIUM ALUMINIDE ALLOYS: SCIENCE AND TECHNOLOGY, P1, DOI 10.1002/9783527636204

[4] High temperature oxidation behavior of laser clad Co-Cr-Mo coating on γ-TiAl substrate [J].

Barekat, Masoud ;

Razavi, Reza Shoja ;

Ghasemi, Ali .

JOURNAL OF LASER APPLICATIONS, 2016, 28 (04)

[5] Nd:YAG laser cladding of Co-Cr-Mo alloy on γ-TiAl substrate [J].

Barekat, Masoud ;

Razavi, Reza Shoja ;

Ghasemi, Ali .

OPTICS AND LASER TECHNOLOGY, 2016, 80 :145-152

[6] High temperature sliding wear behaviour of Inconel 617 and Stellite 6 alloys [J].

Birol, Yucel .

WEAR, 2010, 269 (9-10) :664-671

[7] Microstructure and high-temperature wear resistance of a laser surface alloyed γ-TiAl with carbon [J].

Chen, Y ;

Wang, HM .

APPLIED SURFACE SCIENCE, 2003, 220 (1-4) :186-192

[8] Growth morphologies and mechanism of TiC in the laser surface alloyed coating on the substrate of TiAl intermetallics [J].

Chen, Y ;

Wang, HM .

JOURNAL OF ALLOYS AND COMPOUNDS, 2003, 351 (1-2) :304-308

[9]

Davis J.R., 2000, ASM Specialty Handbook: Nickel, Cobalt, and Their Alloys

[10] Effect of VN alloy addition on the microstructure and wear resistance of Co-based alloy coatings [J].

Ding, Lin ;

Hu, Shengsun ;

Quan, Xiumin ;

Shen, Junqi .

JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 659 :8-14

← 1 2 3 4 →