Mechanical evaluation of polymeric filaments and their corresponding 3D printed samples

3D printing technologies permits to produce functional parts with complex geometries, optimized topologies or enhanced internal structures. The relationship between mechanical performance and manufacturing parameters should be exhaustively analyzed to warrant the long term success of printed products. In this work, the mechanical performance of filaments based on acrylonitrile butadiene styrene (ABS), polylactic acid (PLA) and polylactic acid/polyhydroxyalkanoate (PLA/PHA) was investigated and also compared with their corresponding 3D printed samples. In general, the specimen dimensional deviations were found to be within the tolerances defined by the standard testing protocols. Density values revealed a high level of filament fusion promoting a nearly solid internal structure. The filaments exhibited improved tensile performance with respect to their corresponding printed samples. Tensile and bending performance looked quite independent of the raster angle. Izod impact behavior was increased, for ABS systems printed with the +/- 45 degrees raster orientation. Quasi-static fracture tests displayed improved crack initiation resistance with the 0 degrees/90 degrees raster angle. The crack propagation observed for the +/- 45 degrees specimens, through the bonding of the inter-layers, suggests weak entanglements.