(Y,Tb,Eu)2O3 monospheres for highly fluorescent films and transparent hybrid films with color tunable emission

被引：15

作者：

Zhu, Qi ^{[1
]}

Xiong, Mei ^{[1
]}

Li, Ji-Guang ^{[1
,2
]}

Liu, Weigang ^{[1
]}

Wang, Zhihao ^{[1
]}

Li, Xiaodong ^{[1
]}

Sun, Xudong ^{[1
]}

机构：

[1] Northeastern Univ, Sch Met & Mat, Key Lab Anisotropy & Texture Mat, Minist Educ, Shenyang 110819, Liaoning, Peoples R China

[2] Natl Inst Mat Sci, Adv Mat Proc Unit, Tsukuba, Ibaraki 3050044, Japan

来源：

RSC ADVANCES | 2015年 / 5卷 / 45期

基金：

中国国家自然科学基金;

关键词：

MONODISPERSED COLLOIDAL PARTICLES; SACRIFICIAL TEMPLATE METHOD; PHOTONIC CRYSTALS; PHOTOLUMINESCENCE PROPERTIES; LANTHANIDE COMPOUNDS; LUMINESCENT PROPERTIES; HOLLOW SPHERES; PHOSPHORS; OXIDES; PRECIPITATION;

D O I：

10.1039/c5ra04665c

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

(Y,Tb,Eu)(2)O-3 monospheres (similar to 180 nm in diameter), calcined from the precursors synthesized via urea-based homogeneous precipitation, were employed as the building blocks for highly fluorescent films and as the dispersion fillers for transparent polymer films. The oxide spheres, consisting of similar to 40 nm grains, simultaneously displayed the green emission of Tb3+ at 543 nm and the red emission of Eu3+ at 614 nm under 270 nm UV excitation, with the emission color finely tunable from red to yellow and then to green by increasing the Tb content. The efficiency of Tb3+ -> Eu3+ energy transfer was found to be similar to 51.7% for (Y0.95Tb0.02Eu0.03)(2)O-3. Self-assembling the oxide monospheres produced close-packed phosphor films with transmittance >= 80% (600-850 nm region) and an emission intensity similar to 6.8 times that of the powder form. Meanwhile, solution casting yielded transparent PVA films dispersed with the monospheres, which exhibit outstanding flexibility, high transmittance of >= 80% (450-850 nm region), and multi-color emission. The outcomes of this work may have wide implications for flexible luminescent devices and packaging and energy conversion materials.