On the performance of a highly loadedCO/SiO2 catalyst in the gas phase hydrogenation of crotonaldehyde thermal treatments -: catalyst structure-selectivity relationship

This paper reports on the performance and its relation with the structure of a highly loaded (41 Wt.%) CO/SiO2 catalyst in the gas phase hydrogenation of crotonaldehyde when varying the thermal treatments to which the catalyst precursor has been subjected. The optimum calcination and reduction temperatures were identified where the highest selectivity to crotyl alcohol (around 90%) was obtained with the catalyst calcined at 400 degrees C and reduced at 350 degrees C even at conversions as high as 60%. Higher temperature of calcination was found to lower the crotyl alcohol selectivity. Both, lower and higher reduction temperatures will not favour the crotyl alcohol formation. These results were interpreted and correlated with the surface structure of the catalyst which was shown by temperature programmed reduction (TPR) and X-ray photoelectron spectroscopy (XPS) analysis. Depending on the thermal conditions imposed, the surface consisted of either Co metal, or coexisting metal and its oxide; structure which favours the high crotyl alcohol selectivity. By TEM analysis, large particles (diameter exceeding 50 nm) were identified after reduction at 350 degrees C. A global activation energy of 44 kJ/mol was obtained with this catalyst. In the light of the obtained results a discussion on the reaction mechanism involving metal, metal-oxide double sites has been put forward. It was emphasised that, for selective hydrogenation of crotonaldehyde into unsaturated alcohol, Co catalysts compete favourably with platinum based catalysts. (c) 2004 Elsevier B.V. All rights ieserved.