Influence of the heat input and aging treatment on microstructure and mechanical properties of AISI 317 L steel weldments using 0020 robotic-pulsed GMAW

被引:15
作者
Antunes, P. D. [1 ]
Silva, C. C. [2 ]
Correa, E. O. [3 ]
Tavares, S. S. M. [4 ]
机构
[1] Fed Ctr Technol Educ Minas Gerais CEFET MG, Gen Educ Dept, Varginha, MG, Brazil
[2] Univ Fed Ceara, Welding Res & Technol Lab LPTS, Fortaleza, Ceara, Brazil
[3] Univ Fed Itajuba, Dept Engn Mecan, POB 50, Itajuba, MG, Brazil
[4] Univ Fed Fluminense, Escola Engn, Rua Passo da Patria, Niteroi, RJ, Brazil
关键词
AISI 317L stainless steel; Similar welding; Mechanical and microstructural characterization; SIGMA-PHASE PRECIPITATION; DUPLEX STAINLESS-STEEL; CORROSION-RESISTANCE; WELDED-JOINT; FERRITE; METAL; MORPHOLOGIES; TOUGHNESS; BEHAVIOR;
D O I
10.1007/s00170-019-04621-1
中图分类号
TP [自动化技术、计算机技术];
学科分类号
0812 ;
摘要
In this work, the effect of heat input and aging treatment on the microstructural characteristics and mechanical properties of similar AISI 317L austenitic stainless steel weldments used in the petroleum industry was investigated. The filler metal used was the AWS ER317L electrode at two different heat input levels (4 and 8 kJ/cm) in order to verify the influence of this parameter on the precipitation of deleterious phases. The specimens were aged at 700 degrees C for 50 and 100 h. Quantification and microchemical mapping of precipitated phases after welding and aging thermal treatment (ATT) were performed. Vickers hardness and tensile tests were used to evaluate the mechanical properties. It was observed that aging promoted a refinement of the base metal region, and all delta ferrite was transformed into sigma phase. The delta ferrite present in the fusion zone was completely transformed into sigma and chi phases. In the aged specimens for 100 h a lower occurrence of the secondary austenite phase (gamma 2) was identified, which indicates that with the increase of ATT time the dissolution of gamma 2 occurred in the already precipitated sigma phase. All welding conditions showed an increase in tensile strength, yield limit and hardness with the ATT.
引用
收藏
页码:5151 / 5163
页数:13
相关论文
共 49 条
  • [1] Albuquerque Victor Hugo Costa de, 2007, Matéria (Rio J.), V12, P394, DOI 10.1590/S1517-70762007000200018
  • [2] American Society For Testing And Materials, 1993, STAND PRACT DET SUSC, P262
  • [3] Avelino Jr AF, 2011, THESIS
  • [4] Influence of the ferrite rate on the tenacity of a welded joint in austenitic stainless steel: Experimental study and numerical modelling
    Bouchouicha, B.
    Zemri, M.
    Benguediab, M.
    Imad, A.
    [J]. COMPUTATIONAL MATERIALS SCIENCE, 2009, 45 (02) : 336 - 341
  • [5] Clarification on development of skeletal and lathy ferrite morphologies in stainless steel welds
    Brooks, JA
    Yang, NCY
    Krafcik, JS
    [J]. SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2001, 6 (06) : 412 - 414
  • [6] Low temperature thermal aging of austenitic stainless steel welds: Kinetics and effects on mechanical properties
    Chandra, K.
    Kain, Vivekanand
    Bhutani, Vikas
    Raja, V. S.
    Tewari, R.
    Dey, G. K.
    Chakravartty, J. K.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 534 : 163 - 175
  • [7] Automatic Evaluation of Nickel Alloy Secondary Phases from SEM Images
    de Albuquerque, Victor Hugo C.
    Silva, Cleiton Carvalho
    Menezes, Thiago Ivo de S.
    Farias, Jesualdo Pereira
    Tavares, Joao Manuel R. S.
    [J]. MICROSCOPY RESEARCH AND TECHNIQUE, 2011, 74 (01) : 36 - 46
  • [8] Solidification mode and residual ferrite in low-Ni austenitic stainless steels
    Di Schino, A
    Mecozzi, MG
    Barteri, M
    Kenny, JM
    [J]. JOURNAL OF MATERIALS SCIENCE, 2000, 35 (02) : 375 - 380
  • [9] Chi-phase precipitation in a duplex stainless steel
    Escriba, D. M.
    Materna-Morris, E.
    Plaut, R. L.
    Padilha, A. F.
    [J]. MATERIALS CHARACTERIZATION, 2009, 60 (11) : 1214 - 1219
  • [10] Degradation of mechanical and corrosion resistance properties of AISI 317L steel exposed at 550 °C
    Farneze, H. N.
    Tavares, S. S. M.
    Pardal, J. M.
    do Nascimento, R. F.
    de Abreu, H. F. G.
    [J]. ENGINEERING FAILURE ANALYSIS, 2016, 61 : 69 - 76