Pressureless sintering and properties of Cu/Ti3AlC2 composites

被引：6

作者：

Huang Zhenying ^{[1
]}

Zhai Hongxiang ^{[1
]}

Ai Mingxing ^{[1
]}

Wang Yi ^{[1
]}

Zhang Hongbing ^{[1
]}

机构：

[1] Beijing Jiaotong Univ, Sch Mech & Elect Control Engn, Beijing 100044, Peoples R China

来源：

HIGH-PERFORMANCE CERAMICS V, PTS 1 AND 2 | 2008年 / 368-372卷

关键词：

Cu/Ti3AlC2; pressureless sintering; flexural strength; electrical resistivity;

D O I：

10.4028/www.scientific.net/KEM.368-372.998

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The Cu/Ti3AlC2 composites were fabricated by pressureless sintering a mixture of Ti3AlC2 and copper powders. Their microstructures and properties were investigated. It was found that the molten Cu accelerating the decomposition of Ti3AlC2, inducing the interfacial exfoliation to generate, and forming a sub-micro-layered structure making up of TiCx layers and Cu-Al alloy layers within a Ti3AlC2 grain. The flexural strength of the composites is reduced with the increase of the volume content of Ti3AlC2 from 50 % to 90 %. The highest flexural strength reaches to as high as 915 MPa. The fracture mode was changed from ductile to brittle with increase in the content of Ti3AlC2. The higher flexural strength can be attributed to a stronger interface bond between TiCx and Cu-Al phase. The electrical resistivity and Vickers hardness of the composites were also measured.

引用

页码：998 / 1000

页数：3

共 4 条

[1]

Ai MX, 2006, J AM CERAM SOC, V89, P1114, DOI [10.1111/j.1551-29162005.00818.x, 10.1111/j.1551-2916.2005.00818.x]

[2] A new Ti3AlC2/Cu cermet exhibiting excellent tribological properties [J].

Huang Zhenying ;

Zhai Hongxiang ;

Ai Mingxing .

HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 :1436-1438

[3]

Pietzka MA., 1994, J. Phase Equilib, V15, P392, DOI [10.1007/BF02647559, DOI 10.1007/BF02647559]

[4] Unusual microstructures and strength characteristics of Cu/Ti3AlC2 cermets [J].

Zhai Hong-Xiang ;

Ai Ming-Zing ;

Huang Zhen-Ying ;

Zhou Yang ;

Li Shi-Bo ;

Zhang Zhi-li .

HIGH-PERFORMANCE CERAMICS IV, PTS 1-3, 2007, 336-338 :1394-1396

← 1 →