Does the Application of Additional Hydrophobic Resin to Universal Adhesives Increase Bonding Longevity of Eroded Dentin?

This paper evaluates the effect of an additional hydrophobic resin coat (extra HL) associated with universal adhesives on sound and eroded dentin and evaluated immediately or after 2 years of water storage to improve the microtensile bond strength (mu TBS) and nanoleakage (NL) when compared to the use of universal adhesives only. Sixty-four molars were assigned to eight groups using the following combinations: 1. dentin substrate, including sound and eroded dentin; 2. treatment, including the control and extra HL and storage time (immediately and after two-years of storage). Two universal adhesives (Prime & Bond Active or Scotchbond Universal) were evaluated. Before restoration, half of the teeth were subjected to soft-drink erosion. Composite buildups were bonded; specimens were stored (37 degrees C/24 h), sectioned into resin-dentin bonded sticks and tested for microtensile bond strength and nanoleakage using SEM (immediately and after two-years of storage). Three-way ANOVA and Tukey's test (alpha = 0.05%) were used. In the immediate testing, the application of extra HL did not increase microtensile bond strength values compared with the control group in either substrate (p > 0.05). However, extra HL significantly decreased nanoleakage values when applied to eroded and sound dentin (p = 0.0001). After two years, the application of extra HL produced significantly higher microtensile bond strength and lower nanoleakage values than the control group for both adhesives (p = 0.0001). In all cases, sound dentin showed higher microtensile bond strength and lower nanoleakage values than eroded dentin (p = 0.000001). An extra HL increased the bond strength and reduced nanoleakage in eroded dentin after two-years of storage.