Electrochromic performance of mixed V2O5-MoO3 thin films synthesized by pulsed spray pyrolysis technique

被引：59

作者：

Patil, C. E. ^{[2
]}

Jadhav, P. R. ^{[1
]}

Tarwal, N. L. ^{[1
]}

Deshmukh, H. P. ^{[3
]}

Karanjkar, M. M. ^{[4
]}

Patil, P. S. ^{[1
]}

机构：

[1] Shivaji Univ, Dept Phys, Thin Film Mat Lab, Kolhapur 416004, Maharashtra, India

[2] Bharati Vidyapeeths MBSK Kanya Mahavidyalay, Dept Phys, Sangli, MS, India

[3] Bharati Vidyapeeths YM Coll, Pune, Maharashtra, India

[4] Vivekanand Coll, Kolhapur, Maharashtra, India

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2011年 / 126卷 / 03期

关键词：

Oxides; Semiconductors; Thin films; Optical properties; OPTICAL-PROPERTIES;

D O I：

10.1016/j.matchemphys.2010.12.055

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Mixed V2O5-MoO3 thin films were deposited onto the glass and fluorine doped tin oxide (FTO) coated glass substrates, at 400 degrees C by pulsed spray pyrolysis technique (PSPT). Equimolar vanadium chloride (VCl3) and ammonium molybdate aqueous solutions were mixed together in volume proportions (5-15% molybdenum) and used as a precursor solution for the deposition of mixed V2O5-MoO3 thin films. The structural, morphological, optical and electrochromic properties of the films deposited at different Mo concentrations were studied. With increase in the percentage of Mo the peaks belonging to tetragonal phase of V2O5 eventually disappear and the (1 0 1) orthorhombic V2O5 phase is observed. Scanning electron microscopy (SEM) shows micro thread like reticulated morphology. The optical band gap energy varied over 2.91-2.85 eV. All the films exhibited cathodic electrochromism in lithium containing electrolyte (0.5 M LiClO4 + propylene carbonate (PC)). The highest coloration efficiency (CE) for the V2O5 film with 15% MoO3 mixing was found 35.27 cm(2) C-1. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：711 / 716

页数：6

共 20 条

[11] Properties of mixed-oxide MoO3/V2O5 electrochromic films coated from peroxo-polymolybdovanadate solutions [J].

Li, YM ;

Kudo, T .

SOLAR ENERGY MATERIALS AND SOLAR CELLS, 1995, 39 (2-4) :179-190

[12] Reactive sputtering deposition of V2O5-z on flexible PET/ITO substrates for electrochromic devices [J].

Lin, Yung-Sen ;

Tsai, Chung-Wei .

SURFACE & COATINGS TECHNOLOGY, 2008, 202 (22-23) :5641-5645

[13] Laser-induced colouration of V2O5 [J].

Liu, ZL ;

Fang, GJ ;

Wang, YQ ;

Bai, YD ;

Yao, KL .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2000, 33 (18) :2327-2332

[14] SMALL POLARON TRANSPORT IN AMORPHOUS V2O5 FILMS [J].

MURAWSKI, L ;

SANCHEZ, C ;

LIVAGE, J ;

AUDIERE, JP .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 1990, 124 (01) :71-75

[15] LITHIUM INCORPORATION BY VANADIUM PENTOXIDE [J].

MURPHY, DW ;

CHRISTIAN, PA ;

DISALVO, FJ ;

WASZCZAK, JV .

INORGANIC CHEMISTRY, 1979, 18 (10) :2800-2803

[16] RF sputtered electrochromic V2O5 films [J].

Ottaviano, L ;

Pennisi, A ;

Simone, F ;

Salvi, AM .

OPTICAL MATERIALS, 2004, 27 (02) :307-313

[17] Synthesis of electrochromic vanadium oxide by pulsed spray pyrolysis technique and its properties [J].

Patil, C. E. ;

Tarwal, N. L. ;

Shinde, P. S. ;

Deshmukh, H. P. ;

Patil, P. S. .

JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2009, 42 (02)

[18] Electrochromism in spray deposited iridium oxide thin films [J].

Patil, PS ;

Kawar, RK ;

Sadale, SB .

ELECTROCHIMICA ACTA, 2005, 50 (12) :2527-2532

[19]

PATIL PS, 2008, Patent No. 214163

[20] Structural and optical properties of electrodeposited molybdenum oxide thin films [J].

Patil, R. S. ;

Uplane, M. D. ;

Patil, P. S. .

APPLIED SURFACE SCIENCE, 2006, 252 (23) :8050-8056

← 1 2 →