Magnetic properties and workability of 6.5% Si steel sheet

被引：176

作者：

Haiji, H ^{[1
]}

Okada, K ^{[1
]}

Hiratani, T ^{[1
]}

Abe, M ^{[1
]}

Ninomiya, M ^{[1
]}

机构：

[1] NKK CORP,MAT & PROC RES CTR,KAWASAKI KU,KAWASAKI,KANAGAWA 210,JAPAN

来源：

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS | 1996年 / 160卷

关键词：

amorphous; CVD; iron loss; magnetostriction; siliconizing; 6.5% Si steel; workability;

D O I：

10.1016/0304-8853(96)00128-X

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

NKK led the world in the construction of a continuous production line for manufacturing 6.5% silicon steel sheet in coil form using a CVD siliconizing process. The product is a non-oriented, 6.5% silicon steel sheet with an iron loss of W1/10k = 9.25 W/kg (0.1 mm thick) and excellent soft magnetic properties. The workability of this product was improved by preventing oxidation of the source materials during manufacture. NKK recently succeeded in manufacturing 0.05 mm thick 6.5% silicon steel sheet in coil form. Cut cores from this material have a very low iron loss at high frequencies that is superior to that obtainable with 0.025 mm Fe-based amorphous materials.

引用

页码：109 / 114

页数：6

共 6 条

[1]

GOKYU I, 1955, SILICON STEEL SHEET, P164

[2]

MITANI H, 1967, J JPN MET I, V31, P1341

[3] MAGNETIC-PROPERTIES OF 6.5-PERCENT SI-FE FILAMENT FORMED BY A MODIFIED TAYLOR TECHNIQUE [J].

NARITA, K ;

TESHIMA, N ;

AGANO, T ;

FUNAHASHI, H .

IEEE TRANSACTIONS ON MAGNETICS, 1980, 16 (03) :517-520

[4] CONTINUOUS SILICONIZING TECHNOLOGY OF 6.5-PERCENT SILICON STEEL SHEET [J].

OKAMI, Y ;

ABE, M ;

YAMAJI, T ;

TAKADA, Y ;

NINOMIYA, H .

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1994, 80 (10) :777-782

[5] COMMERCIAL SCALE PRODUCTION OF FE-6.5 WT-PERCENT SI SHEET AND ITS MAGNETIC-PROPERTIES [J].

TAKADA, Y ;

ABE, M ;

MASUDA, S ;

INAGAKI, J .

JOURNAL OF APPLIED PHYSICS, 1988, 64 (10) :5367-5369

[6] MAGNETIC-PROPERTIES AND WORKABILITY OF 6.5-PERCENT SILICON STEEL SHEET MANUFACTURED IN CONTINUOUS CVD SILICONIZING LINE [J].

YAMAJI, T ;

ABE, M ;

TAKADA, Y ;

OKADA, K ;

HIRATANI, T .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1994, 133 (1-3) :187-189

← 1 →