Influence of vapor transport equilibration on spectroscopic parameters of Er3+ in LiNbO3 crystals

A number of X-, Y- and Z-cut Er(/Yb):LiNbO, crystals with six different doping levels of rare earth ions were annealed at 1110 degrees C for 120 h using the vapor transport equilibration (VTE) technique, At room temperature, alpha-polarized or unpolarized absorption spectra of these VTE-treated crystals and corresponding as-grown crystals were recorded in the wavelength range 280 - 1700 nm. The absorption characteristics of the VTE-treated crystals are summarized and compared with those of the as-grown crystals. The (Li+ + RE3)/Nb5+(RE3+ = Er3+ or Er3+ + Yb3+) ratios in the VTE-treated Er(/Yb): LiNbO3 crystals were evaluated using the optical absorption edge or Raman linewidth of the 153 cm, E(TO) phonon. Based upon the measured spectral data, spectroscopic parameters of Er3+ ions in as-grown and VTE-treated crystals were calculated using the Judd-Ofelt (J-O) theory. The influences of Er3+ doping level, type of crystal cut and VTE treatment on the key spectroscopic parameters, including integrated absorption coefficient, oscillator strength, J-O parameters and radiative lifetimes of three dominant emission manifolds (I-4(13/2)(similar to 1530 nm), F-4(9/2) (similar to 660 nm) and S-4(3/2) (similar to 560 nm)), are discussed and summarized and compared with the results for as-grown crystals. The results for as-grown crystals are also compared with those reported previously. The present theoretical result concerning the VTE effect on the 1530 nm lifetime is in rough agreement with the experimental result reported previously. (c) 2005 WILEY-VCH Verlag GmbH & Co, KGaA, Weinheim