Fabrication of a novel Mg-RE (Nd,Ce) intermetallic compound coating by molten salt diffusion and its effect on corrosion resistance of magnesium alloys

被引：9

作者：

Han Baojun ^{[1
,2
]}

Gu Dongdong ^{[2
]}

He Qiong ^{[2
]}

Zhang Xiaolian ^{[1
,2
]}

Peng Guanghuai ^{[1
,2
]}

Yang Chubin ^{[1
,2
]}

机构：

[1] Gannan Normal Univ, Jiangxi Prov Engn Res Ctr Magnesium Alloys, Ganzhou 341000, Peoples R China

[2] Gannan Normal Univ, Sch Chem & Chem Engn, Ganzhou 341000, Peoples R China

来源：

JOURNAL OF RARE EARTHS | 2016年 / 34卷 / 07期

关键词：

intermetallic compounds; AZ91D magnesium alloy; corrosion; rare earth molten salts; AZ91D; SURFACE; PROTECTION; AZ31; ND; MICROSTRUCTURE; BEHAVIOR; AM50;

D O I：

10.1016/S1002-0721(16)60084-4

中图分类号：

O69 [应用化学];

学科分类号：

081704 ;

摘要：

A novel Mg-rare earth (Nd,Ce) coating containing intermetallic compound was fabricated on the surface of the AZ91D magnesium alloy by bathing the sample in a NaCl-KCl-LiCl-NdCl3-CeCl3 molten salt. The cross-sectional morphology, microstructure and phase composition of the coating were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS). The corrosion resistance was characterized by the potentiodynamic polarization curves. The SEM observation indicated that a continuous and compact diffusion coating was obtained on the surface of SMATed AZ91D magnesium alloy and the XRD and TEM investigations revealed that the new phases were Al2Ce and Al2Nd intermetallic. The potentiodynamic polarization curves showed that the Mg-RE coating improved the corrosion resistance of the AZ91D magnesium alloy, and the corrosion current density of the coated sample was about 1510 mA/cm(2) lower than the uncoated sample.

引用

页码：731 / 735

页数：5

共 24 条

[21] A composite anodizing coating containing superfine Al2O3 particles on AZ31 magnesium alloy [J].

Zhang, Dingfei ;

Gou, Yinning ;

Liu, Yuping ;

Guo, Xingxing .

SURFACE & COATINGS TECHNOLOGY, 2013, 236 :52-57

[22] A chromium-free conversion coating of magnesium alloy by a phosphate-permanganate solution [J].

Zhao, M ;

Wu, SS ;

Luo, JR ;

Fukuda, Y ;

Nakae, H .

SURFACE & COATINGS TECHNOLOGY, 2006, 200 (18-19) :5407-5412

[23] Air plasma sprayed thermal barrier coatings on titanium alloy substrates [J].

Zhou, Hong ;

Li, Fei ;

Wang, Bo He Jun ;

Sun, Bao-De .

SURFACE & COATINGS TECHNOLOGY, 2007, 201 (16-17) :7360-7367

[24] Microstructure and properties of the low-power-laser clad coatings on magnesium alloy with different amount of rare earth addition [J].

Zhu, Rundong ;

Li, Zhiyong ;

Li, Xiaoxi ;

Sun, Qi .

APPLIED SURFACE SCIENCE, 2015, 353 :405-413

← 1 2 3 →