Fabrication of a novel Mg-RE (Nd,Ce) intermetallic compound coating by molten salt diffusion and its effect on corrosion resistance of magnesium alloys

被引：9
作者：
Han Baojun [1 ,2 ]
Gu Dongdong [2 ]
He Qiong [2 ]
Zhang Xiaolian [1 ,2 ]
Peng Guanghuai [1 ,2 ]
Yang Chubin [1 ,2 ]
机构：
[1] Gannan Normal Univ, Jiangxi Prov Engn Res Ctr Magnesium Alloys, Ganzhou 341000, Peoples R China
[2] Gannan Normal Univ, Sch Chem & Chem Engn, Ganzhou 341000, Peoples R China
来源：
JOURNAL OF RARE EARTHS | 2016年 / 34卷 / 07期
关键词：
intermetallic compounds; AZ91D magnesium alloy; corrosion; rare earth molten salts; AZ91D; SURFACE; PROTECTION; AZ31; ND; MICROSTRUCTURE; BEHAVIOR; AM50;
D O I：
10.1016/S1002-0721(16)60084-4
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
A novel Mg-rare earth (Nd,Ce) coating containing intermetallic compound was fabricated on the surface of the AZ91D magnesium alloy by bathing the sample in a NaCl-KCl-LiCl-NdCl3-CeCl3 molten salt. The cross-sectional morphology, microstructure and phase composition of the coating were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS). The corrosion resistance was characterized by the potentiodynamic polarization curves. The SEM observation indicated that a continuous and compact diffusion coating was obtained on the surface of SMATed AZ91D magnesium alloy and the XRD and TEM investigations revealed that the new phases were Al2Ce and Al2Nd intermetallic. The potentiodynamic polarization curves showed that the Mg-RE coating improved the corrosion resistance of the AZ91D magnesium alloy, and the corrosion current density of the coated sample was about 1510 mA/cm(2) lower than the uncoated sample.
引用
收藏
页码：731 / 735
页数：5
相关论文
共 24 条
[1]   Role of alloyed Nd in the microstructure and atmospheric corrosion of as-cast magnesium alloy AZ91 [J].
Arrabal, R. ;
Mingo, B. ;
Pardo, A. ;
Matykina, E. ;
Mohedano, M. ;
Merino, M. C. ;
Rivas, A. ;
Maroto, A. .
CORROSION SCIENCE, 2015, 97 :38-48
[2]   Corrosion behaviour of AZ91D and AM50 magnesium alloys with Nd and Gd additions in humid environments [J].
Arrabal, R. ;
Matykina, E. ;
Pardo, A. ;
Merino, M. C. ;
Paucar, K. ;
Mohedano, M. ;
Casajus, P. .
CORROSION SCIENCE, 2012, 55 :351-362
[3]   Effect of Nd on the corrosion behaviour of AM50 and AZ91D magnesium alloys in 3.5 wt.% NaCl solution [J].
Arrabal, R. ;
Pardo, A. ;
Merino, M. C. ;
Mohedano, M. ;
Casajus, P. ;
Paucar, K. ;
Garces, G. .
CORROSION SCIENCE, 2012, 55 :301-312
[4]   Effects of calcium, samarium addition on microstructure and mechanical properties of AZ61 magnesium alloy [J].
Chen Yu'an ;
Jin Li ;
Fang Dan ;
Song Yu ;
Ye Ruiyu .
JOURNAL OF RARE EARTHS, 2015, 33 (01) :86-92
[5]   Characterization and corrosion studies of fluoride conversion coating on degradable Mg implants [J].
Chiu, K. Y. ;
Wong, M. H. ;
Cheng, F. T. ;
Man, H. C. .
SURFACE & COATINGS TECHNOLOGY, 2007, 202 (03) :590-598
[6]   Improvement of the properties of AZ91D magnesium alloy by treatment with a molten AlCl3-NaCl salt to form an Mg-Al intermetallic surface layer [J].
He, Meifeng ;
Liu, Lei ;
Wu, Yating ;
Tang, Zhixin ;
Hu, Wenbin .
JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2009, 6 (03) :407-411
[7]   Corrosion properties of surface-modified AZ91D magnesium alloy [J].
He Meifeng ;
Liu Lei ;
Wu Yating ;
Tang Zhixin ;
Hu Wenbin .
CORROSION SCIENCE, 2008, 50 (12) :3267-3273
[8]  
Herera-Solaz V, 2014, MATER CHARACT, V128, P199
[9]   Corrosion of AZ91D magnesium alloy with a chemical conversion coating and electroless nickel layer [J].
Huo, HW ;
Li, Y ;
Wang, FH .
CORROSION SCIENCE, 2004, 46 (06) :1467-1477
[10]   Chrome-free neodymium-based protective coatings for magnesium alloys [J].
Jin, Guo ;
Yang, Yuyun ;
Cui, Xiufang ;
Liu, Erbao ;
Wang, Zhongyu ;
Li, Qingfen .
MATERIALS LETTERS, 2011, 65 (08) :1145-1147
123