The impact of surfactants on the properties of electroless Ni-P-SiC coatings

The development and properties of electroless nickel silicon (Ni-P-SiC) coatings on steel substrates with different surfactants were investigated in this study. Different surfactant additives (anionic, cationic, and nonionic) were used to prevent the agglomeration of SiC nanoparticles in the coating bath. Their effect on the deposition rate, surface roughness, microhardness, and corrosion resistance of Ni-P-SiC coatings was investigated in this study. XRD, SEM, and EDS analysis was performed to observe the crystal structure, morphology, and chemical composition of the deposit. Potentiodynamic polarization tests, stylus surface measurement devices, and Vickers microhardness testers were used to explore the corrosion behavior, surface roughness, and microhardness of the coatings. The presence of the three surfactants at a 0.6 g/L concentration significantly influences the charac-teristics of the coatings. The maximum number of SiC nanoparticles was homogeneously distributed in the Ni alloy in the presence of a cationic surfactant. The coating developed from the cationic surfactant bath exhibited the highest microhardness, corrosion resistance, deposition rate, and smooth surface identified in the coating developed from the cationic surfactant bath.