Synthesis and thermal properties of the thermosetting resin based on cyano functionalized benzoxazine

A novel thermosetting resin based on cyano functionalized benzoxazine (BZCN) has been synthesized from 2,6-bis(4-diaminobenzoxy)benzonitrile phenol and formaldehyde by solution reaction. The structure of the monomer is supported by FTIR, H-1 NMR and C-13 NMR spectra, which have exhibited that the reactive benzoxazine rings and cyano group exist in the molecular structure of BZCN. The curing reactions of BZCN are monitored by the disappearance of the nitrile peak and the tri-substituted benzene ring that is attached with oxazine ring peak at 2231 and 930 cm(-1), respectively. The complete cured materials could achieve char yields up to 70% at 800 degrees C in nitrogen atmosphere, above 64% at 600 degrees C in air (20% oxygen) environments and the glass transition temperature tip to 250 degrees C. The thermally activated curing polymerization reaction of BZCN follows multiple polymerization mechanisms via the ring-opening polymerization of oxazine rings and the triazine ring-formation of cyano groups, which contribute to the stability of the polymer. (C) 2007 Elsevier Ltd. All rights reserved.