Fabrication and mechanical properties of lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere

被引：2

作者：

Kashihara, Makoto ^{[1
]}

Yonetani, Hirosi ^{[1
]}

Kobi, Takahiro ^{[1
]}

Hyun, Soong-Keun ^{[2
]}

Suzuki, Shinsuke ^{[2
]}

Nakajima, Hideo ^{[2
]}

机构：

[1] Mori Seiki Co Ltd, Iga 5191414, Japan

[2] Osaka Univ, Inst Sci & Ind Res, Suita, Osaka 565, Japan

来源：

TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 2008年 / 94卷 / 01期

关键词：

lotus-type porous carbon steel; nitrogen; porous metals; porosity; unidirectional solidification; tensile test;

D O I：

10.2355/tetsutohagane.94.30

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Lotus-type porous carbon steel (AISI1018) whose long cylindrical pores are aligned in one direction was fabricated by unidirectional solidification in pressurized nitrogen gas. The ingots with the porosity from 10 to 30% were fabricated under the nitrogen gas pressure of 2.5 MPa at various transference velocities from 40 to 160 mu m s(-1). Tensile strength was measured for Lotus-type porous carbon steel. Elongation was improved due to normalizing at 1200K. The yield strength does not change even in lotus steel less than 20% in porosity. This superior property is attributed to nitrogen solid solution hardening and pore existence.

引用

页码：30 / 34

页数：5

共 13 条

[1] Heat transfer capacity of lotus-type porous copper heat sink
Chiba, H
Ogushi, T
Nakajima, H
Ikeda, T
[J]. JSME INTERNATIONAL JOURNAL SERIES B-FLUIDS AND THERMAL ENGINEERING, 2004, 47 (03) : 516 - 521
[2] Fabrication of lotus-type porous iron and its mechanical properties
Hyun, SK
Ikeda, T
Nakajima, H
[J]. SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2004, 5 (1-2) : 201 - 205
[3] Fabrication of porous iron by unidirectional solidification in nitrogen atmosphere
Hyun, SK
Nakajima, H
[J]. MATERIALS TRANSACTIONS, 2002, 43 (03) : 526 - 531
[4] Anisotropic mechanical properties of porous copper fabricated by unidirectional solidification
Hyun, SK
Murakami, K
Nakajima, H
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 299 (1-2): : 241 - 248
[5] Fabrication of Lotus-type porous stainless steel by continuous zone melting technique and mechanical property
Ikeda, T
Aoki, T
Nakajima, H
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (01): : 77 - 86
[6] Fabrication of lotus-type porous stainless steel by unidirectional solidification under hydrogen atmosphere
Ikeda, T
Tsukamoto, M
Nakajima, H
[J]. MATERIALS TRANSACTIONS, 2002, 43 (11) : 2678 - 2684
[7] IKEDA T, 2004, J JPN I LIGHT MET, V54, P388
[8] Fabrication of lotus-type porous carbon steel by unidirectional solidification in nitrogen atmosphere
Kashihara, M
Hyun, SK
Yonetani, H
Kobi, T
Nakajima, H
[J]. SCRIPTA MATERIALIA, 2006, 54 (04) : 509 - 512
[9] KASHIHARA M, 2006, POROUS METALS FORMIN, P215
[10] Fabrication of lotus-type porous carbon steel by the continuous zone melting method and its mechanical properties
Kujime, T
Hyun, SK
Nakajima, H
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2006, 37A (02): : 393 - 398

← 1 2 →