Interface stress induced hardness enhancement and superelasticity in polytetrafluoroethylene/metal multilayer thin films

被引:13
作者
Kusano, E. [1 ]
Kikuchi, N. [1 ]
机构
[1] Kanazawa Inst Technol, Adv Ctr Mat Sci, Yatsukaho, Hakusan 9240838, Japan
关键词
Sputtering; Multilayer thin films; Nanoindentation; Polytetrafluoroethylene; Hardness enhancement; Superelasticity; MECHANICAL-PROPERTIES; YOUNGS MODULUS; SURFACE-ENERGY; INDENTATION; WORK; NANOINDENTATION; DEFORMATION; METALS;
D O I
10.1016/j.tsf.2011.07.034
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Polytetrafluoroethylene (PTFE)/Al, PTFE/Cu, and PTFE/Ti multilayer thin films have been deposited in order to investigate effects of interface energy on mechanical properties. PTFE, which has a low surface energy of 19.2 mJ/m(2), was used to introduce a large interface energy into multilayer thin films. PTFE thin film was deposited by rf magnetron sputtering using a PTFE sheet target. Al, Cu, and Ti were deposited by dc magnetron sputtering. The multilayer thin films were fabricated sequentially without breaking vacuum. Substrate used was aluminosilicate glass. The modulation period was changed from 6.7 to 200 nm. The total thickness was about 200 nm for all samples. The internal stress of metal layers changed from tensile to compressive and increased with decreasing modulation period for all of PTFE/Al, PTFE/Cu, and PTFE/Ti. Both hardness enhancement and superelasticity were observed in the results of nanoindentation measurements. The energy dissipated during nanoindentation process (one load and unload cycle) decreased with decreasing modulation period. The minimum value of the ratio of dissipated/loaded energy was <40%, which is smaller than the values obtained for monolithic PTFE or metal films (about 73% for PTFE and 87% for Al, 72% for Cu, and 71% for Ti, respectively). This meant that the PTFE/metal nano-multilayer thin films became more elastic with decreasing modulation period. The tendency of change in the mechanical properties strongly correlated to internal stress. Mechanisms involved in anomalous behaviors in film hardness and elasticity were discussed based on the relationship to interface energy, interface stress, and internal stress, induced by multilayering of the films. It is concluded that a large compressive stress introduced in the thin films increased the energy needed to deform elastically or plastically the thin film during indentation, resulting in the increase in hardness and elasticity. The nanoindentation analysis of the multilayer thin films emphasized that in PTFE/metal multilayer thin films mechanical properties of the films depend on interface stress induced by the accumulated interface energy, being independent of bulk materials properties composing thin films, resulting in increase in hardness and elasticity. (C) 2011 Elsevier B.V. All rights reserved.
引用
收藏
页码:404 / 412
页数:9
相关论文
共 37 条
[1]  
Alkorta J, 2006, J MATER RES, V21, P302, DOI [10.1557/jmr.2006.0009, 10.1557/JMR.2006.0009]
[2]   Dislocation-based deformation mechanisms in metallic nanolaminates [J].
Anderson, PM ;
Foecke, T ;
Hazzledine, PM .
MRS BULLETIN, 1999, 24 (02) :27-33
[3]  
BARNETT SA, 1994, ANNU REV MATER SCI, V24, P481
[4]  
Brandrup J., 2005, POLYM HDB, P36
[5]  
Brandrup J., 2005, POLYM HDB, P526
[6]   SURFACE AND INTERFACE STRESS EFFECTS IN THIN-FILMS [J].
CAMMARATA, RC .
PROGRESS IN SURFACE SCIENCE, 1994, 46 (01) :1-38
[7]   Stresses in multilayered thin films [J].
Cammarata, RC ;
Bilello, JC ;
Greer, AL ;
Sieradzki, K ;
Yalisove, SM .
MRS BULLETIN, 1999, 24 (02) :34-38
[8]   Relation between the ratio of elastic work to the total work of indentation and the ratio of hardness to Young's modulus for a perfect conical tip [J].
Chen, J. ;
Bull, S. J. .
JOURNAL OF MATERIALS RESEARCH, 2009, 24 (03) :590-598
[9]   Scaling, relationships for indentation measurements [J].
Cheng, YT ;
Li, ZY ;
Cheng, CM .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 2002, 82 (10) :1821-1829
[10]   Relationships between hardness, elastic modulus, and the work of indentation [J].
Cheng, YT ;
Cheng, CM .
APPLIED PHYSICS LETTERS, 1998, 73 (05) :614-616