Effect of pre-oxidation on the hot corrosion of CoNiCrAlYRe alloy

被引：39
作者：
Chen, L-C [1 ]
Zhang, C. [1 ]
Yang, Z-G [1 ]
机构：
[1] Tsinghua Univ, State Key Lab New Ceram & Fine Proc, Dept Mat Sci & Engn, Beijing 100084, Peoples R China
来源：
CORROSION SCIENCE | 2011年 / 53卷 / 01期
关键词：
Alloy; Oxidation; Hot corrosion; THERMAL-BARRIER COATINGS; OXIDATION BEHAVIOR; BASE SUPERALLOY; SCALES; RESISTANCE; MECHANISM; RHENIUM; TESTS;
D O I：
10.1016/j.corsci.2010.09.045
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of pre-oxidation on the resistance to hot corrosion was examined by corroding the CoNiCrAlYRe alloy at 900 degrees C in molten Na2SO4 Preoxidized specimens featured strong adhesion of oxide scale with uniform multi-layered structure The time of pre-oxidation was crucial for controlling Al content sufficient for subsequent hot corrosion However direct corrosion yielded a defective and non-protective oxide scale which allowed detrimental penetration of sulfur into substrate Sulfur migrating along phase boundary was trapped by yttrium to diminish slightly sulphidation Thus two advantages of proper pre-oxidation treatment were presented as keeping repairing for Al2O3 scale and inhibiting sulfur penetration (C) 2010 Elsevier Ltd All rights reserved
引用
收藏
页码：374 / 380
页数：7
相关论文
共 25 条
  • [11] LIH W, 1991, OXID MET, V36, P221, DOI 10.1007/BF00662963
  • [12] The effect of preoxidation atmosphere on oxidation behavior and thermal cycle life of thermal barrier coatings
    Matsumoto, Mineaki
    Hayakawa, Kazuyuki
    Kitaoka, Satoshi
    Matsubara, Hideaki
    Takayama, Hiroshi
    Kagiya, Yukio
    Sugita, Yuuji
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 441 (1-2): : 119 - 125
  • [13] Effect of Y distribution on the oxidation kinetics of NiCoCrAlY bond coat alloys
    Nijdam, T. J.
    Sloof, W. G.
    [J]. OXIDATION OF METALS, 2008, 69 (1-2): : 1 - 12
  • [14] Inhibition of interdiffusion from MCrAlY overlay coatings by application of a Ni-Re interlayer
    Page, RA
    Leverant, GR
    [J]. JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 1999, 121 (02): : 313 - 319
  • [15] The hot corrosion behaviour of HVOF sprayed MCrAIX coatings under Na2SO4 (+NaCl) salt films
    Pahlavanyali, S
    Sabour, A
    Hirbod, M
    [J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2003, 54 (09): : 687 - 693
  • [16] THE OXIDATION MECHANISM OF THETA-AL2O3 SCALES
    PINT, BA
    MARTIN, JR
    HOBBS, LW
    [J]. SOLID STATE IONICS, 1995, 78 (1-2) : 99 - 107
  • [17] Rapp R.A., 1981, MOLTEN SALTS, V1, P159
  • [18] Simons E.L., 1955, Corrosion, V11, P505
  • [19] THE OXIDATION BEHAVIOR OF SOME FECRALY, FECRAL, AND YTTRIUM ION-IMPLANTED FECRAL ALLOYS COMPARED AND CONTRASTED
    SMEGGIL, JG
    SHUSKUS, AJ
    [J]. JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A-VACUUM SURFACES AND FILMS, 1986, 4 (06): : 2577 - 2582
  • [20] NATURE OF INDIGENOUS SULFURE SEGREGATED TO THE FREE METAL-SURFACE AND TO THE SCALE METAL INTERFACE
    SMEGGIL, JG
    PETERSON, GG
    [J]. OXIDATION OF METALS, 1988, 29 (1-2): : 103 - 119
123