Effect of pre-oxidation on the hot corrosion of CoNiCrAlYRe alloy

被引：38
|
作者：
Chen, L-C [1 ]
Zhang, C. [1 ]
Yang, Z-G [1 ]
机构：
[1] Tsinghua Univ, State Key Lab New Ceram & Fine Proc, Dept Mat Sci & Engn, Beijing 100084, Peoples R China
来源：
CORROSION SCIENCE | 2011年 / 53卷 / 01期
关键词：
Alloy; Oxidation; Hot corrosion; THERMAL-BARRIER COATINGS; OXIDATION BEHAVIOR; BASE SUPERALLOY; SCALES; RESISTANCE; MECHANISM; RHENIUM; TESTS;
D O I：
10.1016/j.corsci.2010.09.045
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of pre-oxidation on the resistance to hot corrosion was examined by corroding the CoNiCrAlYRe alloy at 900 degrees C in molten Na2SO4 Preoxidized specimens featured strong adhesion of oxide scale with uniform multi-layered structure The time of pre-oxidation was crucial for controlling Al content sufficient for subsequent hot corrosion However direct corrosion yielded a defective and non-protective oxide scale which allowed detrimental penetration of sulfur into substrate Sulfur migrating along phase boundary was trapped by yttrium to diminish slightly sulphidation Thus two advantages of proper pre-oxidation treatment were presented as keeping repairing for Al2O3 scale and inhibiting sulfur penetration (C) 2010 Elsevier Ltd All rights reserved
引用
收藏
页码：374 / 380
页数：7
相关论文
共 50 条
  • [1] Improving hot corrosion resistance of aluminized TiAl alloy by anodization and pre-oxidation
    Hu, Yuan-tao
    Zheng, Lei
    Yan, Hao-jie
    Wu, Lian-kui
    Lin, Xiang-jun
    Cao, Fa-he
    Jiang, Mei-yan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2021, 31 (01) : 193 - 206
  • [2] Effect of Pre-Oxidation Treatment on Corrosion Resistance of FeCoSiBPC Amorphous Alloy
    Zhang, Qian
    Hui, Xidong
    Li, Zongzhen
    Zhang, Guangqiang
    Lin, Jingcheng
    Li, Xuelian
    Zheng, Wei
    Cao, Xia
    Zhou, Shaoxiong
    MATERIALS, 2022, 15 (09)
  • [3] Hot Corrosion Behavior of Ti45Al8.5Nb Alloy: Effect of Anodization and Pre-oxidation
    Yan, Hao-Jie
    Xia, Jun-Jie
    Wu, Lian-Kui
    Cao, Fa-He
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2022, 35 (09) : 1531 - 1546
  • [4] Hot Corrosion Behavior of Ti45Al8.5Nb Alloy: Effect of Anodization and Pre-oxidation
    Hao-Jie Yan
    Jun-Jie Xia
    Lian-Kui Wu
    Fa-He Cao
    Acta Metallurgica Sinica (English Letters), 2022, 35 : 1531 - 1546
  • [5] Hot Corrosion Behavior of Ti45Al8.5Nb Alloy: Effect of Anodization and Pre-oxidation
    Hao-Jie Yan
    Jun-Jie Xia
    Lian-Kui Wu
    Fa-He Cao
    ActaMetallurgicaSinica(EnglishLetters), 2022, 35 (09) : 1531 - 1546
  • [6] The effect of pre-oxidation on the hot corrosion behavior of CoNiCrAlHf alloy in Na2SO4 environment at elevated temperature
    Ali, Rawaid
    Song, Peng
    Khan, Muhammad
    Huang, Taihong
    Ali, Shabir
    Sha, Syed Hatim
    Lu, Jiansheng
    Ul Wahab, Zain
    Pervaiz, Seemab
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2022, 128 (09):
  • [7] The effect of pre-oxidation on the hot corrosion behavior of CoNiCrAlHf alloy in Na2SO4 environment at elevated temperature
    Rawaid Ali
    Peng Song
    Muhammad Khan
    Taihong Huang
    Shabir Ali
    Syed Hatim Sha
    Jiansheng Lu
    Zain Ul Wahab
    Seemab Pervaiz
    Applied Physics A, 2022, 128
  • [8] Effect of platinum and pre-oxidation on the hot corrosion behavior of aluminide coating with NaCl at 1050 °C
    Peng, Jubo
    Huang, Taihong
    Song, Peng
    Huang, Wenlang
    He, Yang
    Ma, Tao
    Yang, Bixiao
    Liang, Yuwei
    Wu, Minxuan
    Chen, Rong
    MATERIALS RESEARCH EXPRESS, 2020, 7 (11)
  • [9] Effect of pre-oxidation on hot corrosion of Ni-Cr-Al alloy in molten Na2SO4-NaCl
    Hara, Motoi
    Okumura, Hirobumi
    Nakagawa, Tokiko
    Sato, Yoshiyuki
    Shinata, Yutaka
    Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, 1995, 59 (12): : 1259 - 1265
  • [10] Effect of pre-oxidation on hot corrosion of Ni-Cr-Al alloy in molten Na2SO4-NaCl
    Hara, M
    Okumura, H
    Nakagawa, T
    Sato, Y
    Shinata, Y
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1995, 59 (12) : 1259 - 1265
12345