Advanced thermal gradient mechanical fatigue testing of CMSX-4 with an oxidation protection coating

被引:32
作者
Baufeld, Bernd [1 ,2 ]
Bartsch, Marion [2 ]
Heinzelmann, Michael [3 ]
机构
[1] Katholieke Univ Leuven, B-3001 Louvain, Belgium
[2] German Aerosp Ctr, D-51147 Cologne, Germany
[3] Univ Appl Sci Bonn Rhein Sieg, D-53359 Rheinbach, Germany
关键词
defects; cracks; stress analysis; superalloys; thermomechanical fatigue/cycling;
D O I
10.1016/j.ijfatigue.2007.01.034
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Frequently, turbine blades are cooled internally, which generates thermal gradients over the blade wall and, consequently, multi-axial stresses in addition to stresses due to centrifugal forces. In order to study these conditions, a new thermal gradient mechanical fatigue (TGMF) testing equipment with a lamp furnace has been developed. The advantages of this furnace are high power (16 lamps a 1000 W), controlled thermal gradients, high heating and cooling rates, and lamp lives exceeding 8000 thermal cycles. The studied material system was the single-crystal line superalloy CMSX-4 with a NiPtAl oxidation protection Coating. Different TGMF tests with a maximal surface temperature of 1050 degrees C, mechanical loads up to 400 MPa, and cycle numbers up to 9000 resulted in microstructural changes and defects, reflecting in each case the particular temperature, thermal gradient, and local stresses. For example, phase evolution of the metal coatings and rafting of the gamma/gamma' substrate morphology was investigated. Furthermore, cracks at the inner specimen surface and at substrate pores were detected. The observed morphology and defects were related to the applied thermomechanical loads using finite element calculations. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码:219 / 225
页数:7
相关论文
共 28 条
[1]   Rafting prediction criterion for superalloys under a multiaxial stress [J].
Arrell, DJ ;
Valles, JL .
SCRIPTA MATERIALIA, 1996, 35 (06) :727-732
[2]  
Bartsch M, 1999, ADV ENG MATER, V1, P127, DOI 10.1002/(SICI)1527-2648(199910)1:2<127::AID-ADEM127>3.0.CO
[3]  
2-6
[4]  
BARTSCH M, IN PRESS INT J FATIG
[5]   Defect evolution in thermal barrier coating systems under multi-axial thermomechanical loading [J].
Baufeld, B ;
Bartsch, M ;
Dalkiliç, S ;
Heinzelmann, M .
SURFACE & COATINGS TECHNOLOGY, 2005, 200 (5-6) :1282-1286
[6]   Microstructural changes as postmortem temperature indicator in Ni-Co-Cr-Al-Y oxidation protection coatings [J].
Baufeld, B ;
Bartsch, M ;
Broz, P ;
Schmücker, M .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 384 (1-2) :162-171
[7]   Rafting in monocrystalline nickel-base superalloys induced by shot peening [J].
Biermann, H ;
Tetzlaff, U ;
von Grossmann, B ;
Mughrabi, H ;
Schulze, V .
SCRIPTA MATERIALIA, 2000, 43 (09) :807-812
[8]  
Biermann H, 1996, SUPERALLOYS 1996, P201
[9]   Determination of local strains in a monocrystalline turbine blade by microbeam X-ray diffraction with synchrotron radiation [J].
Biermann, H ;
Von Grossmann, B ;
Ungár, T ;
Mechsner, S ;
Souvorov, A ;
Drakopoulos, M ;
Snigirev, A ;
Mughrabi, H .
ACTA MATERIALIA, 2000, 48 (09) :2221-2230
[10]  
Biermann H., 1999, URSACHEN AUSWIRKUNGE