Examples of actual defects in high pressure pipelines and probabilistic assessment of residual life for different types of pipeline steels

被引：2

作者：

Cerny, Ivo ^{[1
]}

Mikulova, Dagmar ^{[1
]}

Sis, Jiri ^{[1
]}

机构：

[1] SVUM As, Tovarni 2053, Celakovice 25088, Czech Republic

来源：

3RD INTERNATIONAL SYMPOSIUM ON FATIGUE DESIGN AND MATERIAL DEFECTS (FDMD 2017) | 2017年 / 7卷

关键词：

High pressure pipelines; defects; fatigue crack growth; probabilistic assessment; LARGE COMPONENTS; RAILWAY AXLES; GROWTH; CRACKS; HIDA;

D O I：

10.1016/j.prostr.2017.11.109

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

During recent internal inspection of an operated high pressure pipeline of the diameter DN700, distinct, quite large indications of cracks were found in one of the pipe sections. A part of the section was taken from the ground for a comprehensive experimental programme containing analyses of the defect type, dimensions and character and also fatigue test at variable internal pressure with the maximum value corresponding to real operation. The analysed defects mostly occurred during pipe manufacture followed by stress corrosion cracking mechanism in some cases. An existence of fatigue crack growth (FCG) during fatigue pressure test in some cases was demonstrated. Within another experimental programme, an extensive measurement of FCG rates in different high pressure pipeline steels was performed. The evaluated data enabled to carry out serious statistical evaluation. Probabilistic assessment of residual life of pipes made of different steels, containing semi elliptical external surface axial crack was carried out using ALIAS HIDA software developed within the European Framework Programme project. Copyright (C) 2017 The Authors. Published by Elsevier B.V.

引用

页码：431 / 437

页数：7

共 22 条

[1]

[Anonymous], 2015, P 27 PIP PIGG INT MA

[2]

Bagaviev A., 2004, P C PROB LIF CRACK A

[3] Probabilistic fatigue assessment for railway axles and derivation of a simple format for damage calculations [J].

Beretta, S. ;

Regazzi, D. .

INTERNATIONAL JOURNAL OF FATIGUE, 2016, 86 :13-23

[4]

Bielak O., 2004, P C PROB LIF CRACK A

[5] An evaluation of the resistance of pipeline steels to initiation and early growth of stress corrosion cracks [J].

Cerny, I ;

Linhart, V .

ENGINEERING FRACTURE MECHANICS, 2004, 71 (4-6) :913-921

[6] The use of DCPD method for measurement of growth of cracks in large components at normal and elevated temperatures [J].

Cerny, I .

ENGINEERING FRACTURE MECHANICS, 2004, 71 (4-6) :837-848

[7]

Cerny I, 2001, INT J PRES VES PIP, V78, P893, DOI 10.1016/S0308-0161(01)00104-1

[8]

Cerny I., 1993, WIT T ENG SCI, V2, P239

[9]

Cerny I, 2004, P 4 INT C PROB LIF C

[10] Assessment of industrial components in high temperature plant using the "ALIAS-HIDA" - A case study [J].

Deschanels, H ;

Escaravage, C ;

Thiry, JM ;

Hamata, NL ;

Colantoni, D .

ENGINEERING FAILURE ANALYSIS, 2006, 13 (05) :767-779

← 1 2 3 →