Accumulative spin-bonding (ASB) as a novel SPD process for fabrication of nanostructured tubes

被引:110
作者
Mohebbi, M. S. [1 ]
Akbarzadeh, A. [1 ]
机构
[1] Sharif Univ Technol, Dept Mat Sci & Engn, Tehran, Iran
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2010年 / 528卷 / 01期
关键词
Accumulative spin-bonding (ASB); Severe plastic deformation (SPD); Tube spinning; Nanostructured tubes; Zener-Hollomon parameter; EBSD; ULTRAFINE-GRAINED ALUMINUM; STRAIN-RATE SENSITIVITY; MECHANICAL-PROPERTIES; PLASTIC-DEFORMATION; FLOW; EVOLUTION; METALS; MICROSTRUCTURE; ARB;
D O I
10.1016/j.msea.2010.08.081
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A novel SPD process for manufacturing of high strength tubes and cylinders by accumulative spin-bonding (ASB) is proposed. It is demonstrated that due to incremental deformation in this process, high strain rate without considerable temperature rise is achieved. This is accompanied with a high value of Zener-Hollomon parameter as a characteristic of this SPD process. ASB was applied to a commercially pure aluminum up to four cycles and its effects on the microstructure and mechanical properties were examined by optical microscopy, TEM, EBSD, microhardness and tension tests. The results show that ultra-fine grains are developed during the process by formation of subgrains at early stages followed by increase of the misorientations at later stages. This leads to a nanostructure with average grain thickness and length of 186 and 419 nm, respectively. It is indicated that while the hardness of outer regions is more than the inner ones, the hardness and its homogeneity is increased with the ASB cycles. Periodical presence of external layers within the thickness and consequent hardness saturation are responsible for this hardness evolution. As a result of grain refinement and the scheme of hardness development, the yield and tensile strength of material are significantly increased. Moreover, the ratio of the yield strength to the tensile strength and consequently the uniform elongation is decreased with the ASB cycles. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码:180 / 188
页数:9
相关论文
共 25 条
[1]  
*ASM, 1993, ASM HDB, V2
[2]   A dislocation-based model for all hardening stages in large strain deformation [J].
Estrin, Y ;
Toth, LS ;
Molinari, A ;
Brechet, Y .
ACTA MATERIALIA, 1998, 46 (15) :5509-5522
[3]  
Gil-Sevillano J, 1981, PROG MATER SCI, V25, P69
[4]   PLASTIC-FLOW INSTABILITY UNDER COMPRESSIVE LOADING DURING SHEAR SPINNING PROCESS [J].
GUR, M ;
TIROSH, J .
JOURNAL OF ENGINEERING FOR INDUSTRY-TRANSACTIONS OF THE ASME, 1982, 104 (01) :17-22
[5]  
Hayama M., 1966, B FAC ENG YOKOHAMA U, V15, P33
[6]  
Hosford W., 1993, METAL FORMING MECH M, V2nd
[7]   Microstructural evolution during accumulative roll-bonding of commercial purity aluminum [J].
Huang, X ;
Tsuji, N ;
Hansen, N ;
Minamino, Y .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 340 (1-2) :265-271
[8]  
Humphreys F.J., 2005, RECRYSTALLIZATION RE
[9]   Microstructures and mechanical properties of 6061 aluminum alloy processed by accumulative roll-bonding [J].
Lee, SH ;
Saito, Y ;
Sakai, T ;
Utsunomiya, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 325 (1-2) :228-235
[10]   Evolution of microstructure for multilayered Al/Ni composites by accumulative roll bonding process [J].
Min, Guanghui ;
Lee, Jung-Moo ;
Kang, Suk-Bong ;
Kim, Hyung-Wook .
MATERIALS LETTERS, 2006, 60 (27) :3255-3259