Study on high performance warm compacted Fe-2Ni-2Cu-1Mo-1C powder metallurgy materials

被引：1

作者：

Xiao, Zhiyu ^{[1
]}

Wang, Jun ^{[1
]}

Luo, Shuhua ^{[1
]}

Wen, Lipin ^{[1
]}

Li, Yuanyuan ^{[1
]}

机构：

[1] S China Univ Technol, Coll Mech Engn, Guangzhou 510640, Peoples R China

来源：

PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4 | 2007年 / 353-358卷

关键词：

warm compaction; ferrous material; warm compacting behavior; mechanical property;

D O I：

10.4028/www.scientific.net/KEM.353-358.1621

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Warm compacting and sintering behaviors of pre-mixed Fe-2Ni-2Cu-1Mo-1C powders were studied. Results showed that green density increased with compacting temperature and then fell slightly; the maximum green density was obtained at about 120 degrees C. Green compact density and spring back effect of the pre-mixed powder increased gradually as the compacting pressure increased. Sintered density first increased and then fell as the temperatures went up under different sintering temperatures for 50 minutes, but the trends of sintering dilatation were first reduced and then increased. Sintered density first reduced and then increased with the prolonged sintering time at 1300 degrees C, but the trends of dimension change after sintering were the very reverse. Tensile strength, elongation and hardness of the warm compacted Fe-2Ni-2Cu-1Mo-1C materials generally increased as sintering temperature and sintering time went up.

引用

页码：1621 / 1624

页数：4

共 8 条

[1] Warm compaction of metal powders: why it works, why it requires a sophisticated engineering approach [J].

Bocchini, GF .

POWDER METALLURGY, 1999, 42 (02) :171-180

[2]

CAPUS J, 1997, METAL POWDER REPORT, V61, P19

[3]

Degoix CN, 1998, INT J POWDER METALL, V34, P29

[4]

ENGSTROEM U, 1994, POWDER METALL, V37, P57

[5]

PETER J, 1997, POWDER METALLURGY IN, V33, P37

[6]

SHIVANATH R, 1996, ADV PM PARTICULATE M, P427

[7]

[肖志瑜 XIAO Zhiyu], 2006, [中国有色金属学报, The Chinese Journal of Nonferrous Metals], V16, P1326

[8] A study on warm compacting behaviors of 316L stainless steel powder [J].

Xiao, ZY ;

Ke, MY ;

Chen, WP ;

Ni, DH ;

Li, YY .

ADVANCES IN MATERIALS MANUFACTURING SCIENCE AND TECHNOLOGY, 2004, 471-472 :443-447

← 1 →