Properties of Mg/graphite and Mg/graphene as cathode electrode on primary cell battery

Since graphene was first isolated in 2004, it has become an attractive material on electrochemical energy storage devices. The purpose of this study is to compare Mg/graphite and Mg/graphene electrodes to commercial primary battery cathodes. This research is an experimental laboratory research. Graphene was synthesized with Hummer's method modified. Electrodes cathode of primary battery (Mg/graphite and Mg/graphene) were prepared using impregnation method. Graphene and electrodes cathode were analyzed with X-Ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive X-Ray (SEM-EDX) and conductivity, respectively. The XRD data of graphene show that there is a weak and sharp peak on 2 theta = 26,5 degrees, indicating graphene is formed. The peaks shape of 2 theta = 35 degrees are totally different for Mg/graphite and Mg/graphene. At Mg/graphite, the sharp and narrow peak appears on 2 theta = 35 degrees. It means Mg is well deposited on graphite. Interestingly, Mg/graphene has narrow and weak peak on 2 theta = 35 degrees, indicating the Mg was deposited on graphene and properties of Mg has been changed by graphene. This data is also well confirmed by EDX data. Mg atoms exist on graphene (1.47 wt%) (EDX data). SEM images of Mg/graphite and Mg/graphene are significantly different, probably support material effect. The properties of Mg/graphite and Mg/graphene comparing to commercial primary battery cathode were evaluated using conductivity. The conductivity of Mg/graphene (1080 mu S/cm) is highest among Mg/graphite (90 mu S/cm) and commercial battery cathode (10 mu S/cm). All of data show that the Mg/graphene is potentially used as a primary battery cathode.