Formation of TiB2 by volume combustion and mechanochemical process

被引:39
作者
Bilgi, Eda [1 ]
Camurlu, H. Erdem [2 ]
Akgun, Baris [1 ]
Topkaya, Yavuz [1 ]
Sevinc, Naci [1 ]
机构
[1] Middle E Tech Univ, Dept Met & Mat Engn, TR-06531 Ankara, Turkey
[2] Akdeniz Univ, Dept Mech Engn, TR-07058 Antalya, Turkey
关键词
ceramics; chemical synthesis; X-ray diffraction;
D O I
10.1016/j.materresbull.2007.05.001
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Titanium diboride was produced both by volume combustion synthesis (VCS) and by mechanochemical synthesis (MCP) through the reaction of TiO2, B2O3 and Mg. VCS products, expected to be composed of TiB2 and MgO, were found to contain also side products such as Mg2TiO4, Mg3B2O6, MgB2 and TiN. HCl leaching was applied to the reaction products with the objective of removing MgO and the side products. Formation of TiN could be prevented by conducting the VCS under an argon atmosphere. Mg2TiO4 did not form when 40% excess Mg was used. Wet ball milling of the products before leaching was found to be effective in removal of Mg3B2O6 during leaching in I M HCl. When stoichiometric starting mixtures were used, all of the side products could be removed after wet ball milling in ethanol and leaching in 5 M HCl when pure TiB2 was obtained with a molar yield of 30%. Pure TiB2 could also be obtained at a molar yield of 45.6% by hot leaching of VCS products at 75 degrees C in 5 M HCl, omitting the wet ball milling step. By MCP, products containing only TiB2 and MgO were obtained after 15 h of ball milling. Leaching in 0.5 M HCl for 3 min was found to be sufficient for elimination of MgO. Molar yield of TiB2 was 89.6%, much higher than that of VCS. According to scanning electron microscope analyses, the TiB2 produced had average grain size of 0.27 +/- 0.08 mu m. (C) 2007 Elsevier Ltd. All rights reserved.
引用
收藏
页码:873 / 881
页数:9
相关论文
共 24 条
[1]   Synthesis and characterization of TiB2-reinforced iron-based composites [J].
Anal, A ;
Bandyopadhyay, TK ;
Das, K .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 172 (01) :70-76
[2]  
[Anonymous], 1980, PHYS CHEM HIGH TEMPE
[3]   THE VAPOR-PHASE DEPOSITION OF REFRACTORY MATERIALS .1. GENERAL CONDITIONS AND APPARATUS [J].
CAMPBELL, IE ;
POWELL, CF ;
NOWICKI, DH ;
GONSER, BW .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1949, 96 (05) :318-333
[4]  
Cullity B.D., 2001, Elements of X-ray Diffraction, V3rd ed., P169
[5]   Effect of HO concentration on TiB2 separation from a self-propagating high-temperature synthesis (SHS) product [J].
Demircan, Umut ;
Derin, Bora ;
Yucel, Onuralp .
MATERIALS RESEARCH BULLETIN, 2007, 42 (02) :312-318
[6]   KINETICS OF THE COMBUSTION SYNTHESIS OF TIB2 [J].
HOLT, JB ;
KINGMAN, DD ;
BIANCHINI, GM .
MATERIALS SCIENCE AND ENGINEERING, 1985, 71 (1-2) :321-327
[7]  
Kaptay G., 1999, Plasmas Ions, V2, P45, DOI DOI 10.1016/S1288-3255(00)87686-8
[8]  
Kim J. J., 1985, CERAM ENG SCI P, V6, P1313
[9]   Oxidation behavior of titanium boride at elevated temperatures [J].
Koh, YH ;
Lee, SY ;
Kim, HE .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (01) :239-241
[10]   Oxidation of TiB2 powders below 900 degrees C [J].
Kulpa, A ;
Troczynski, T .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1996, 79 (02) :518-520