The structural and mechanical properties of (CeO2)(1-x)(GdO1.5)(x) electrolytes

被引：31

作者：

Sammes, N ^{[1
]}

Tompsett, G ^{[1
]}

Zhang, YJ ^{[1
]}

Cartner, A ^{[1
]}

Torrens, R ^{[1
]}

机构：

[1] UNIV WAIKATO,DEPT CHEM,HAMILTON,NEW ZEALAND

来源：

DENKI KAGAKU | 1996年 / 64卷 / 06期

关键词：

(CeO2)(1-x)(GdO1.5)(x) electrolytes; solid oxide fuel cell; mechanical properties;

D O I：

10.5796/kogyobutsurikagaku.64.674

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

(CeO2)(1-x) (GdO1.5)(x) is a possible candidate as an electrolyte in a low temperature solid oxide fuel cell. This paper describes how Raman spectroscopy can be used to determine the structural changes observed with increasing Gd2O3 dopant concentration. The mechanical properties of (CeO2)(0.8) (GdO1.5)(0.2) were also determined. The 4-point bend strength, for example, was found to be 143 +/- 10.4 MPa at room temperature, and 114.7 +/- 11.9 MPa at 800 degrees C. The paper also describes several methods for determining the fracture toughness of (CeO2)(0.8) (GdO1.5)(0.2) at room temperature.

引用

收藏

页码：674 / 680

页数：7

相关论文

共 21 条

[1] MECHANICAL-PROPERTIES OF DOPED CUBIC ZIRCONIA CERAMICS [J].

ABRAHAM, I ;

GRITZNER, G .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1993, 12 (13) :995-997

[2] MECHANICAL-PROPERTIES OF LOW-TEMPERATURE SINTERED CERIA TETRAGONAL ZIRCONIA POLYCRYSTALS .2. FRACTURE-TOUGHNESS [J].

ANNAMALAI, VE ;

PONRAJ, R ;

IYER, SR ;

GOKULARATHNAM, CV ;

KRISHNAMURTHY, R .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1993, 12 (09) :671-673

[3] A CRITICAL-EVALUATION OF INDENTATION TECHNIQUES FOR MEASURING FRACTURE-TOUGHNESS .1. DIRECT CRACK MEASUREMENTS [J].

ANSTIS, GR ;

CHANTIKUL, P ;

LAWN, BR ;

MARSHALL, DB .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (09) :533-538

[4]

BADWAL SPS, 1993, BCH STEELE SCI TECHN, P713

[5] SYNTHESIS AND CHARACTERIZATION OF (CEO2)(0.8)(SMO1.5)(0.2) THIN-FILMS FROM POLYMERIC PRECURSORS [J].

CHEN, CC ;

NASRALLAH, MM ;

ANDERSON, HU .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1993, 140 (12) :3555-3560

[6] STUDY OF A SOLID OXIDE FUEL-CELL WITH A CERIA-BASED SOLID ELECTROLYTE [J].

INOUE, T ;

SETOGUCHI, T ;

EGUCHI, K ;

ARAI, H .

SOLID STATE IONICS, 1989, 35 (3-4) :285-291

[7] MIXED ELECTRICAL-CONDUCTION IN FLUORITE-TYPE CE1-XGDXO2-X/2 [J].

KUDO, T ;

OBAYASHI, H .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1976, 123 (03) :415-419

[8] NEW FORMULA FOR INDENTATION TOUGHNESS IN CERAMICS [J].

LAUGIER, MT .

JOURNAL OF MATERIALS SCIENCE LETTERS, 1987, 6 (03) :355-356

[9] CHARACTERIZATION OF 3-DIMENSIONAL THROUGH-THICKNESS TRANSFORMATION ZONE IN 9-MOL-PERCENT-CE-TZP CERAMICS [J].

LIU, T .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1994, 77 (08) :2203-2206

[10] ENHANCED CERIA - A LOW-TEMPERATURE SOFC ELECTROLYTE [J].

MARICLE, DL ;

SWARR, TE ;

KARAVOLIS, S .

SOLID STATE IONICS, 1992, 52 (1-3) :173-182