NEW TYPES OF UNFAVORABLE NONMETALLIC INCLUSIONS BASED ON MgO-Al2O3 AND METALLURGICAL FACTORS GOVERNING THEIR CONTENT IN METAL. PART 2. TRANSFORMATION MECHANISMS FOR NONMETALLIC INCLUSIONS BASED ON ALUMINA MAGNESIA SPINEL. MAIN APPROACHES MAKING IT POSSIBLE TO REDUCE THE CONTENT OF THE INCLUSIONS IN QUESTION IN STEEL

被引:0
作者
Zaitsev, A. I. [1 ]
Rodionova, I. G. [1 ]
Semernin, G. V. [1 ]
Shaposhnikov, N. G. [1 ]
Kazankov, A. Yu. [1 ]
机构
[1] Bardin Cent Res Inst Ferrous Met, Moscow, Russia
基金
俄罗斯基础研究基金会;
关键词
low-alloy carbon steels; corrosion-active non-metallic inclusions; ladle treatment; reaction with lining; slag;
D O I
10.1007/s11015-011-9405-7
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The main mechanisms are considered for formation and transformation of non-metallic inclusions based on alumina magnesia spinel, and the unfavorable effect on corrosion resistance of carbon and low-alloy steels in aqueous chlorine-containing media. Basic approaches are demonstrated making it possible to reduce the content of the inclusions in question in steel aimed both at reducing the content of inclusions during steel smelting, and on limiting the possibility of their transformation during steel continuous casting and hot rolling.
引用
收藏
页码:149 / 157
页数:9
相关论文
共 11 条
[1]  
LEMANN J, 2006, MET MAT T, V24, P351
[2]  
RODIONOVA IG, 2005, CORROSION ACTIVE NON, P15
[3]  
RODIONOVA IG, 2005, STAL, P86
[4]  
RODIONOVA IG, 2009, CORROSION GRADES STE, P2
[5]  
RODIONOVA IG, 2004, RUSS METALL+, P3
[6]  
RYBAKOVA OV, 1999, COLL ULTRAFINE CONDI
[7]  
SHAKOLSKAYA ML, 1979, CRYSTALS
[8]  
Shaposhnikov N. G., 2004, MATERIALOVEDENIE, P2
[9]  
SIROTIN YI, 1979, BASES CRYSTAL CHEM
[10]  
Villars P., PAULING FILE BINARIE