Properties of AA7075 aluminum alloy in aging and retrogression and reaging process

被引：73

作者：

Ozer, Gokhan ^{[1
]}

Karaaslan, Ahmet ^{[1
]}

机构：

[1] Yildiz Tech Univ, Dept Met & Mat Engn, Fac Chem & Met Engn, TR-34210 Istanbul, Turkey

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2017年 / 27卷 / 11期

关键词：

aluminum alloy; precipitate behavior; retrogression and reaging; impact toughness; hardness; electrical conductivity; ZN-MG ALLOY; EXFOLIATION CORROSION; AL; STRENGTH; MICROSTRUCTURE; PRECIPITATION; EVOLUTION; BEHAVIOR; MODEL;

D O I：

10.1016/S1003-6326(17)60261-9

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

A retrogression process was applied to AA7075 alloy at 180, 240 and 320 degrees C for 1, 30, 50, 70, 90 and 120 min. After the retrogression, aging treatment was reapplied with T6 conditions (120 degrees C, 24 h). The mechanical properties of aged samples were determined by V-Charpy and hardness tests and also, physical properties of samples were determined by electrical conductivity tests. Moreover, microstructural properties were characterized by light microscope and transmission electron microscope. The results show that the effects of the temperature and the duration of the retrogression and reagent on the impact toughness and hardness are related to the precipitates at the grain boundary.

引用

页码：2357 / 2362

页数：6

共 29 条

[1] CALORIMETRIC STUDIES OF 7000 SERIES ALUMINUM-ALLOYS .2. COMPARISON OF 7075, 7050, AND RX720 ALLOYS
ADLER, PN
DEIASI, R
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1977, 8 (07): : 1185 - 1190
[2] Effect of solution heat treatment on galvanic coupling between intermetallics and matrix in AA7075-T6
Andreatta, F
Terryn, H
de Wit, JHW
[J]. CORROSION SCIENCE, 2003, 45 (08) : 1733 - 1746
[3] CHANGES IN SOLID-SOLUTION COMPOSITION AS A FUNCTION OF ARTIFICIAL AGING TIME FOR ALUMINUM ALLOY-7075
BARTGES, CW
[J]. JOURNAL OF MATERIALS SCIENCE LETTERS, 1994, 13 (11) : 776 - 778
[4] Characterization of the mechanical properties changes in an Al-Zn-Mg alloy after a two-step ageing treatment at 70° and 135 °C
Chemingui, Mahmoud
Khitouni, Mohamed
Jozwiak, Karol
Mesmacque, Gerard
Kolsi, Abdelwaheb
[J]. MATERIALS & DESIGN, 2010, 31 (06) : 3134 - 3139
[5] Cina B.M., 1974, US Patent, P12, Patent No. 3856584
[6] A TEM STUDY OF MICROSTRUCTURAL CHANGES DURING RETROGRESSION AND REAGING IN 7075 ALUMINUM
DANH, NC
RAJAN, K
WALLACE, W
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1983, 14 (09): : 1843 - 1850
[7] Influence of quench and heating rates on the ageing response of an Al-Zn-Mg-(Zr) alloy
Deschamps, A
Brechet, Y
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 251 (1-2): : 200 - 207
[8] Esmailian M., 2015, INT J CHEM MOL NUCL, V9-11, P1230
[9] The Effect of the Surface Treating and High-Temperature Aging on the Strength and SCC Susceptibility of 7075 Aluminum Alloy
Fooladfar, Hamidreza
Hashemi, Babak
Younesi, Mousa
[J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2010, 19 (06) : 852 - 859
[10] Evolution of Grain Boundary Precipitates in Al 7075 Upon Aging and Correlation with Stress Corrosion Cracking Behavior
Goswami, Ramasis
Lynch, Stanley
Holroyd, N. J. Henry
Knight, Steven P.
Holtz, Ronald L.
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2013, 44A (03): : 1268 - 1278

← 1 2 3 →