Nanocrystalline metals go ductile under shear deformation

被引:15
作者
Ames, Markus [1 ]
Grewer, Manuel [1 ]
Braun, Christian [1 ]
Birringer, Rainer [1 ]
机构
[1] Univ Saarland, Expt Phys FR7 2, D-66041 Saarbrucken, Germany
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2012年 / 546卷
关键词
Shear deformation; Activation volume; Strain-hardening rate; Nanocrystalline metals; Plasticity; MOLECULAR-DYNAMICS SIMULATION; GRAIN-BOUNDARY MOTION; PLASTIC-DEFORMATION; MECHANICAL-BEHAVIOR; ACTIVATION VOLUME; RATE SENSITIVITY; GLASSES; SIZE; DISLOCATIONS; TEMPERATURE;
D O I
10.1016/j.msea.2012.03.061
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Nanocrystalline Pd90Au10 (grain size <10 nm) has been deformed under dominant shear and superimposed compression to large plastic strains (epsilon> 20%). Taking stress strain curves at different strain rates (10(-4) < epsilon < 10(0)) allowed us to extract the shear activation volume and strain rate sensitivity as a function of plastic strain, which are of the order of 4b(3) and 0.035, respectively. Particularly, the plastic strain-dependent shear activation volume evolves through a maximum value, which relates to yielding. Analyzing the strain hardening rate Theta as a function of applied stress enables to determine strain rate dependent macroyield stresses. Scaling of the applied stress with the macroyield stress yields in addition also the strain rate dependent onset stresses of microyield. Surprisingly, strain hardening associated with interfacial deformation modes dominates the stage of microplasticity, whereas, in the macroplastic regime the strain hardening rate saturates at strains >10% to approach a more or less generic value of Theta/G = 0.015. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:248 / 257
页数:10
相关论文
共 66 条
  • [1] Unraveling the nature of room temperature grain growth in nanocrystalline materials
    Ames, Markus
    Markmann, Juergen
    Karos, Rudolf
    Michels, Andreas
    Tschoepe, Andreas
    Birringer, Rainer
    [J]. ACTA MATERIALIA, 2008, 56 (16) : 4255 - 4266
  • [2] Mechanical testing via dominant shear deformation of small-sized specimen
    Ames, Markus
    Markmann, Juergen
    Birringer, Rainer
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 528 (01): : 526 - 532
  • [3] Argon A, 2008, STRENGTHENING MECH C
  • [4] The strongest size
    Argon, A. S.
    Yip, S.
    [J]. PHILOSOPHICAL MAGAZINE LETTERS, 2006, 86 (11) : 713 - 720
  • [5] DEVELOPMENT OF VISCO-PLASTIC DEFORMATION IN METALLIC GLASSES
    ARGON, AS
    SHI, LT
    [J]. ACTA METALLURGICA, 1983, 31 (04): : 499 - 507
  • [6] A NEW MECHANISM OF WORK-HARDENING IN THE LATE STAGES OF LARGE-STRAIN PLASTIC-FLOW IN FCC AND DIAMOND CUBIC-CRYSTALS
    ARGON, AS
    HAASEN, P
    [J]. ACTA METALLURGICA ET MATERIALIA, 1993, 41 (11): : 3289 - 3306
  • [7] PLASTIC-DEFORMATION IN METALLIC GLASSES
    ARGON, AS
    [J]. ACTA METALLURGICA, 1979, 27 (01): : 47 - 58
  • [8] Mechanistic models for the activation volume and rate sensitivity in metals with nanocrystalline grains and nano-scale twins
    Asaro, RJ
    Suresh, S
    [J]. ACTA MATERIALIA, 2005, 53 (12) : 3369 - 3382
  • [9] Ashby M.F., 1982, DEFORMATION MECH MAP
  • [10] Interface stress in nanocrystalline materials
    Birringer, R
    Hoffmann, M
    Zimmer, P
    [J]. ZEITSCHRIFT FUR METALLKUNDE, 2003, 94 (10): : 1052 - 1061