Bone bonding ability behavior of some ternary borate glasses by immersion in sodium phosphate solution

被引：90

作者：

Abdelghany, A. M. ^{[1
]}

ElBatal, H. A. ^{[2
]}

EzzElDin, F. M. ^{[3
]}

机构：

[1] Natl Res Ctr, Dept Spect, Cairo, Egypt

[2] Natl Res Ctr, Glass Res Dept, Cairo, Egypt

[3] Natl Ctr Radiat Res & Technol, Nasr City, Cairo, Egypt

来源：

CERAMICS INTERNATIONAL | 2012年 / 38卷 / 02期

关键词：

Borate glass; IR spectroscopy; Corrosion weight loss; Sodium phosphate solution; Hydroxyapatite; Bone bonding ability; GAMMA-RAY INTERACTION; BINARY OXIDE MELTS; CHEMICAL DURABILITY; BOROSILICATE GLASSES; THERMAL-EXPANSION; SILICATE-GLASSES; PHASE-SEPARATION; MECHANISMS; CONVERSION; CORROSION;

D O I：

10.1016/j.ceramint.2011.08.038

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Some ternary borate glasses of varying compositions were prepared and corrosion behaviors of such ternary borate glasses after immersion in aqueous dilute phosphate solution were studied using different immersion times. Fourier transform infrared (FTIR) absorption spectral measurements were done before and after immersion in the mentioned solution for extended times up to 3 days to justify the appearance of the characteristic FT infrared bands due to calcium phosphate (hydroxyapatite (HA)) which is considered as the potential indication of bone bonding ability. Experimental IR data confirm the beginning of the appearance of FTIR bands at about 580 and 650 cm(-1) after 1 day and the complete resolution with its characteristic split form after 3 days and more. The corrosion behavior of the studied borate glasses is explained in relation to a suggested hydrolysis and direct dissolution mechanism. The ease of dissolution of all the borate glasses constituents explains the rapid conversion and formation of hydroxyapatite within the borate glass matrix as indicated and confirmed by X-ray diffraction. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

引用

页码：1105 / 1113

页数：9

共 59 条

[1] [Anonymous], 1997, P 2 INT C BOR GLASS
[2] Aluminoborate and aluminoboro silicate glasses with high chemical durability and the effect Of P2O5 additions on the properties
Bengisu, M.
Brow, R. K.
Yimaz, E.
Mogus-Milankovic, A.
Reis, S. T.
[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 2006, 352 (32-35) : 3668 - 3676
[3] BRAY PJ, 1997, P 2 INT C BOR GLASS, P1
[4] Modifier coordination and phosphate glass networks
Brow, RK
Click, CA
Alam, TM
[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 2000, 274 (1-3) : 9 - 16
[5] BROW RK, 1992, Patent No. 5104738
[6] Effect of borate glass composition on its conversion to hydroxyapatite and on the proliferation of MC3T3-E1 cells
Brown, Roger F.
Rahaman, Mohamed N.
Dwilewicz, Agatha B.
Huang, Wenhai
Day, Delbert E.
Li, Yadong
Bal, B. Sonny
[J]. JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A, 2009, 88A (02) : 392 - 400
[7] Budd S.M., 1961, PHYS CHEM GLASS, V2, P115
[8] MOLECULAR MECHANISMS FOR CORROSION OF SILICA AND SILICATE-GLASSES
BUNKER, BC
[J]. JOURNAL OF NON-CRYSTALLINE SOLIDS, 1994, 179 : 300 - 308
[9] AQUEOUS CORROSION OF SODA-SILICA AND SODA-LIME-SILICA GLASS
CLARK, DE
DILMORE, MF
ETHRIDGE, EC
HENCH, LL
[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1976, 59 (1-2) : 62 - 65
[10] Day DE, 2003, GLASS TECHNOL, V44, P75

← 1 2 3 4 5 6 →