Manganese ferrite synthesized from Mn(II) acetate plus hematite freeze-dried powders

被引：19
作者：
Bellini, J. V. [1 ]
de Medeiros, S. N. [1 ]
Ponzoni, A. L. L. [1 ]
Longen, F. R. [1 ]
de Melo, M. A. C. [1 ]
Paesano, A., Jr. [1 ]
机构：
[1] Univ Estadual Maringa, Dept Fis, BR-87020900 Maringa, Parana, Brazil
来源：
MATERIALS CHEMISTRY AND PHYSICS | 2007年 / 105卷 / 01期
关键词：
freeze-drying; manganese ferrite; thermal analysis; Mossbauer spectroscopy;
D O I：
10.1016/j.matchemphys.2007.04.005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Freeze-drying was used to obtain a homogeneous fine powder containing (CH3COO)(2)Mn-2H2O and ct-Fe2O3 (molar ratio Fe:Mn = 3: 1), which was thermally treated for 2 h in N-2 atmosphere, at 400 degrees C. This composite system was further annealed for 4 h in the same atmosphere, either at 700 degrees C or at 1000 degrees C. The 700 degrees C annealed sample was thermally treated in air at 1200 degrees C and then rapidly quenched. The phase transformations that occurred in the freeze-dried and heat-treated powders were investigated by thermal analyses, X-ray diffractometry, scanning electron microscopy and Mossbauer spectroscopy. Results showed that MnO-alpha-Fe2O3-Fe3O4 compounds were obtained after the first heat-treatment. Samples subsequently annealed in N atmosphere revealed the formation of Fe-rich manganese ferrites and manganowUstite phases. However, a single spinel phase was obtained for the sample that had been annealed and quenched in air. (c) 2007 Elsevier B.V. All rights reserved.
引用
收藏
页码：92 / 98
页数：7
相关论文
共 28 条
  • [21] KINETIC AND MECHANISTIC STUDY OF THE NONISOTHERMAL DECOMPOSITION OF MANGANESE(II) ACETATE TETRAHYDRATE
    MOHAMED, MA
    HALAWY, SA
    [J]. THERMOCHIMICA ACTA, 1994, 242 : 173 - 186
  • [22] Structural-chemical transformations of α-Fe2O3 upon transport reduction
    Murin, IV
    Smirnov, VM
    Voronkov, GP
    Semenov, VG
    Povarov, VG
    Sinel'nikov, BM
    [J]. SOLID STATE IONICS, 2000, 133 (3-4) : 203 - 210
  • [23] Newkirk A. E., 1971, Thermochimica Acta, V2, P1, DOI 10.1016/0040-6031(71)85021-9
  • [24] THERMAL AND CHEMICAL EVENTS IN THE DECOMPOSITION COURSE OF MANGANESE COMPOUNDS
    NOHMAN, AKH
    ISMAIL, HM
    HUSSEIN, GAM
    [J]. JOURNAL OF ANALYTICAL AND APPLIED PYROLYSIS, 1995, 34 (02) : 265 - 278
  • [25] Mechano synthesis and process characterization of nanostructured manganese ferrite
    Padella, F
    Alvani, C
    La Barbera, A
    Ennas, G
    Liberatore, R
    Varsano, F
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2005, 90 (01) : 172 - 177
  • [26] Effect of foreign cation of Zn(II) or Mn(II) ion in FeO-wustite on its disproportionation reaction below 575°C
    Sano, T
    Tsuji, M
    Tamaura, Y
    [J]. SOLID STATE IONICS, 1997, 104 (3-4) : 311 - 317
  • [27] PREPARATION OF MANGANESE FERRITE FINE PARTICLES FROM AQUEOUS-SOLUTION
    TANG, ZX
    SORENSEN, CM
    KLABUNDE, KJ
    HADJIPANAYIS, GC
    [J]. JOURNAL OF COLLOID AND INTERFACE SCIENCE, 1991, 146 (01) : 38 - 52
  • [28] Neural network approximation of iron oxide reduction process
    Wiltowski, T
    Piotrowski, K
    Lorethova, H
    Stonawski, L
    Mondal, K
    Lalvani, SB
    [J]. CHEMICAL ENGINEERING AND PROCESSING-PROCESS INTENSIFICATION, 2005, 44 (07) : 775 - 783
123