Subsolidus phase equilibria and the Li5Nd4FeO10 phase in the Li2O-Nd2O3Fe2O system

被引：3
作者：
Ban, I
Drofenik, M
Suvorov, D
Makovec, D
机构：
[1] Univ Maribor, Fac Chem & Chem Engn, SLO-2000 Maribor, Slovenia
[2] Jozef Stefan Inst, Ljubljana 1000, Slovenia
来源：
MATERIALS RESEARCH BULLETIN | 2005年 / 40卷 / 10期
关键词：
differential scanning calorimetry (DSC); thermogravimetric analysis (TGA); X-ray diffraction; magnetic properties; phase equilibrium;
D O I：
10.1016/j.materresbull.2005.04.045
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A survey of the subsolidus phase equilibria in the system Li2O-Nd2O3-Fe2O3 was made at subsolidus temperatures in the range 1000-1050 degrees C. A ternary phase was identified. The phase is centered on Li5Nd4FeO10, with a cubic lattice a = 11.9494 angstrom. The compound melts incongruently at 1105 degrees C. The magnetic susceptibility was measured in the temperature range 4-300 K. The compound is paramagnetic in the temperature range 150-300 K and follows the Curie-Weiss law. At about T-N = 10 K, a long-range magnetic ordering is observed. (C) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1856 / 1863
页数：8
相关论文
共 50 条
  • [41] Subsolidus phase relations in CaO-In2O3-B2O3 system and crystal structure of CaInBO4
    Li, H. K.
    Cai, G. M.
    Fan, J. J.
    Jin, Z. P.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 516 : 107 - 112
  • [42] Ternary system Li20-K2O-Nb2O5 Part I:: Phase equilibria around the lithium niobate existence field
    Cochez, M
    Ferriol, M
    Pöppl, L
    Polgár, K
    Péter, A
    JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 386 (1-2) : 238 - 245
  • [43] Phase stability study of the pseudobinary system Gd2O3-Nd2O3 (T≙1350°C)
    G. A. Costa
    C. Artini
    A. Ubaldini
    M. M. Carnasciali
    P. Mele
    R. Masini
    Journal of Thermal Analysis and Calorimetry, 2008, 92 : 101 - 104
  • [44] XRD investigations in the Nd2O3-Y2O3 system and structural studies of a stabilized monoclinic phase
    Chavan, S. V.
    Achary, S. N.
    Tyagi, A. K.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 441 (1-2) : 332 - 336
  • [45] Phase equilibria of the TiO2-Y2O3 system
    Gong, Weiping
    Li, Dajian
    Chen, Zhongshen
    Zheng, Feng
    Liu, Yong
    Du, Yong
    Huang, Baiyun
    CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2009, 33 (03): : 624 - 627
  • [46] Crystallization and Phase Equilibria in the Tb2O3–Ga2O3 System
    Yu. P. Udalov
    R. M. Rakhmankulov
    T. Yu. Chemekova
    O. L. Belousova
    Glass Physics and Chemistry, 2003, 29 : 200 - 201
  • [47] Phase stability study of the pseudobinary system Gd2O3-Nd2O3 (T≤1350°C)
    Costa, G. A.
    Artini, C.
    Ubaldini, A.
    Carnasciali, M. M.
    Mele, P.
    Masini, R.
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2008, 92 (01) : 101 - 104
  • [48] Dual effect of ZrO2 on phase separation and crystallization in Li2O-Al2O3-SiO2-P2O5 glasses
    Zhu, Lifan
    Wang, Mingzhong
    Xu, Yinsheng
    Zhang, Xianghua
    Lu, Ping
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2022, 105 (09) : 5698 - 5710
  • [49] New Solid Solution and Phase Equilibria in the Subsolidus Area of the Three-Component CuO-V2O5-Ta2O5 Oxide System
    Dabrowska, Grazyna
    Filipek, Elzbieta
    Tabero, Piotr
    MATERIALS, 2022, 15 (01)
  • [50] Subsolidus Phase Relations in the ZnO-BaO-V2O5 System
    郑萌
    吕佩文
    陈达贵
    颜峰波
    黄丰
    结构化学, 2013, 32 (01) : 106 - 112
12345