Pitting on the crevice wall prior to crevice corrosion: Iron in sulfate/chromate solution

被引:18
作者
Shu, Hung-Kai [2 ]
Al-Faqeer, Faisal M. [3 ]
Pickering, Howard W. [1 ]
机构
[1] Penn State Univ, Dept Mat Sci & Engn, University Pk, PA 16802 USA
[2] Natl Taiwan Univ, Dept Mat Sci & Engn, Taipei, Taiwan
[3] Ctr Res & Dev, Dhahran 31311, Saudi Arabia
关键词
Localized corrosion; IR voltage; Polarization curve; Hydrogen evolution; Corrosion product; LOCALIZED CORROSION; STAINLESS-STEEL; MECHANISM; INITIATION; PH;
D O I
10.1016/j.electacta.2010.10.013
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Experimental results are presented for the induction period that precedes the onset of crevice corrosion. In situ visual examination and ex situ microscopy revealed that the first corrosive attack on the (passive) crevice wall occurs as a pit near the bottom of the crevice. Additional pits and corrosion product form higher and higher on the crevice wall during the induction period. The measured current is initially low in the passive range (10 mu A), increasing gradually, but the measured current does not record the large increases in anodic current that produce the pits. The latter result and the observation that gas bubbles form within the pits indicate that the pitting initially is a local cell process of metal dissolution and cathodic reactions on the sample, including H-2 formation which occurs inside the pits in this iron/sulfate-chromate solution (pH 8.8, room temperature). Then, a transition from merging pits to corrosive attack across the width of the crevice wall occurs accompanied by a much steeper increasing current. This latter morphology (horizontal boundary that moves up the wall towards the crevice opening, heaviest attack just below this boundary and passive crevice wall above this boundary) is representative of stable crevice corrosion of the IR type reported in the literature. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码:1719 / 1728
页数:10
相关论文
共 46 条
[41]   Investigation of crevice corrosion susceptibility of L80-13Cr in CO2 solution containing SO2 [J].
Yuan, Yu ;
Jia, Runze ;
Hao, Pengfei ;
Zhang, Fengyu ;
Zhao, Yongyang ;
Li, Chen ;
Xiang, Yong .
INTERNATIONAL JOURNAL OF GREENHOUSE GAS CONTROL, 2025, 141
[42]   Insight into the stress corrosion cracking mechanism of N80 carbon steel under different crevice opening dimensions in a CO2-saturated NaCl solution [J].
Zhang, Xiaoshun ;
Li, Yizhou ;
Cui, Zhongyu ;
Cui, Hongzhi .
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2025, 34 :1410-1423
[43]   In Situ Electrochemical Monitoring of the Crevice Corrosion Process of the 7075-T651 Aluminium Alloy in Acidic NaCl and NaNO3 Solution [J].
Wang, Shengjie ;
Cao, Yamin ;
Liu, Xiaohang ;
Cai, Guangyi .
MATERIALS, 2023, 16 (07)
[44]   The role of acetic acid or H+ in initiating crevice corrosion of N80 carbon steel in CO2-saturated NaCl solution [J].
Li, Y. Z. ;
Xu, N. ;
Guo, X. P. ;
Zhang, G. A. .
CORROSION SCIENCE, 2017, 128 :9-22
[45]   Effect of thiosulphate/H2S on crevice corrosion behaviour of P110 carbon steel in CO2-saturated solution [J].
Dong, Lijin ;
Zhang, Xiaolong ;
Li, Yifeng ;
Wang, Qinying ;
Liu, Li ;
Zheng, Huaibei .
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2020, 55 (03) :253-267
[46]   Inhibition effect of imidazoline inhibitor on the crevice corrosion of N80 carbon steel in the CO2-saturated NaCl solution containing acetic acid [J].
Li, Y. Z. ;
Xu, N. ;
Guo, X. P. ;
Zhang, G. A. .
CORROSION SCIENCE, 2017, 126 :127-141