Electrochemical response of mild steel in ferrous ion enriched and CO2 saturated solutions

被引：33

作者：

Bian, Chen ^{[1
,2
]}

Wang, Zi Ming ^{[1
]}

Han, Xia ^{[1
]}

Chen, Changfeng ^{[2
]}

Zhang, Jian ^{[1
,3
]}

机构：

[1] Sinopec Petr Engn Corp, Dongying 257026, Peoples R China

[2] China Univ Petr Being, Coll Sci, Beijing 102249, Peoples R China

[3] China Univ Petr East China, Coll Oil & Gas Storage & Transportat Engn, Qingdao 266580, Peoples R China

来源：

CORROSION SCIENCE | 2015年 / 96卷

基金：

中国博士后科学基金;

关键词：

Mild steel; EIS; Polarization; Acid corrosion; Interface; CARBON-DIOXIDE CORROSION; PIPELINE STEELS; OIL; BEHAVIOR; GROWTH; FILMS; WATER; PRODUCT;

D O I：

10.1016/j.corsci.2015.03.015

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

To elucidate the role of ferrous ion in CO2 corrosion, the electrochemical behavior of mild steel samples in CO2-saturated brine solutions with various concentrations of ferrous ion were systematically investigated. An apparent inhibition effect was observed with increasing the concentration of ferrous ion and the immersion times. Ferrous ion would initially suppress the cathodic reaction activity by surface adsorption, and then promote the formation of corrosion product layers. A ferrous ion adsorption triggered re-deposition mechanism was proposed to explain the nucleation of FeCO3 layer during CO2 corrosion. Finally, a mechanistic process of CO2 corrosion was clearly presented. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：42 / 51

页数：10

共 40 条

[1] INFLUENCE OF FE2+ ION ON THE CORROSION OF CARBON-STEEL [J].

AAL, MSA ;

WAHDAN, MH ;

GOMMA, GK .

MATERIALS CHEMISTRY AND PHYSICS, 1995, 39 (04) :290-297

[2]

[Anonymous], INITIATION GROWTH ME

[3] Imaging concentration profiles of redox-active species in open-circuit corrosion processes with the scanning electrochemical microscope [J].

Bastos, AC ;

Simoes, AM ;

González, S ;

González-García, Y ;

Souto, RM .

ELECTROCHEMISTRY COMMUNICATIONS, 2004, 6 (11) :1212-1215

[4] Effect of FeCO3 Supersaturation and Carbide Exposure on the CO2 Corrosion Rate of Carbon Steel [J].

Berntsen, T. ;

Seiersten, M. ;

Hemmingsen, T. .

CORROSION, 2013, 69 (06) :601-613

[5] THE EFFECTS OF BICARBONATE ON THE CORROSION AND PASSIVATION OF IRON [J].

DAVIES, DH ;

BURSTEIN, GT .

CORROSION, 1980, 36 (08) :416-422

[6] Effects of pipeline corrosion on the injection water quality of low permeability in oilfield [J].

Dong, Bin ;

Xu, Ying ;

Deng, Hao ;

Luo, Fan ;

Jiang, Shengjian .

DESALINATION, 2013, 326 :141-147

[7]

Dugstad A., 1998, CORROSION, P98031

[8] Electrochemical evaluation of the corrosion behaviour of API-X100 pipeline steel in aerated bicarbonate solutions [J].

Eliyan, Faysal Fayez ;

Mandi, El-Sadig ;

Alfantazi, Akram .

CORROSION SCIENCE, 2012, 58 :181-191

[9] The growth mechanism of CO2 corrosion product films [J].

Gao, M. ;

Pang, X. ;

Gao, K. .

CORROSION SCIENCE, 2011, 53 (02) :557-568

[10] A study of double stranded DNA adsorption on aluminum surface by means of electrochemical impedance spectroscopy [J].

Heli, H. .

COLLOIDS AND SURFACES B-BIOINTERFACES, 2014, 116 :526-530

← 1 2 3 4 →