Studies on atomic layer deposition of IRMOF-8 thin films

Deposition of IRMOF-8 thin films by atomic layer deposition was studied at 260-320 degrees C. Zinc acetate and 2,6-naphthalenedicarboxylic acid were used as the precursors. The as-deposited amorphous films were crystallized in 70% relative humidity at room temperature resulting in an unknown phase with a large unit cell. An autoclave with dimethylformamide as the solvent was used to recrystallize the films into IRMOF-8 as confirmed by grazing incidence x-ray diffraction. The films were further characterized by high temperature x-ray diffraction (HTXRD), field emission scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), time-of-flight elastic recoil detection analysis (TOF-ERDA), nanoindentation, and energy-dispersive x-ray spectroscopy. HTXRD measurements revealed similar behavior to bulk IRMOF-8. According to TOF-ERDA and FTIR, composition of the films was similar to IRMOF-8. Through-porosity was confirmed by loading the films with palladium using Pd(thd)(2) (thd = 2,2,6,6-tetramethyl-3,5-heptanedionato) as the precursor. (C) 2014 American Vacuum Society.