Mechanical and Thermal Failure Induced by Contact between a Li1.5Al0.5Ge1.5(PO4)3 Solid Electrolyte and Li Metal in an All Solid-State Li Cell

被引:240
作者
Chung, Habin [1 ]
Kang, Byoungwoo [1 ]
机构
[1] Pohang Univ Sci & Technol POSTECH, Dept Mat Sci & Engn MSE, Pohang 790784, Gyeongbuk, South Korea
关键词
ELECTROCHEMICAL PROPERTIES; IONIC-CONDUCTIVITY; ENERGY-STORAGE; LITHIUM; BATTERIES; CHALLENGES; INSIGHTS; ANODES;
D O I
10.1021/acs.chemmater.7b02301
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Chemical reactions at the solid electrolyte (SE) and Li metal interface form an interphase before electrochemical reactions occur. This study investigates the effects of the chemically formed interphase between Li metal and Li1.5Al0.5Ge1.5(PO4)(3) (LAGP) on cell failures under various experimental conditions. LAGP forms a black interphase by chemically reacting with Li metal. The interphase comprises a stoichiometrically changed LAGP and Li-related oxides and behaves as a mixed ionic and electronic conductor with the electronic conductivity dominating. Thus, upon application of an electrical current to Li metal anode, most of the Li ions can be reduced at the SE side surface of the interphase rather than the Li metal side, causing a local volumetric increase that triggers cracks in the SE. This crack formation process continues the pulverization of SE, leading to a gradual increase in cell resistance. Under cell operating conditions, electrochemical reactions with the chemically formed interphase can lead to the mechanical deterioration of the SE, leading to cell failure. Furthermore, the chemically formed interphase between melted Li and LAGP above 200 degrees C induces a rigorous chemical reaction with Li that leads to a thermal runaway. The chemical stability of the SE against Li metal can strongly affect the solid-state cells electrical properties, mechanical integrity, and thermal stability.
引用
收藏
页码:8611 / 8619
页数:9
相关论文
共 24 条
[1]   Increase in grain boundary ionic conductivity of Li1.5Al0.5Ge1.5(PO4)3 by adding excess lithium [J].
Chung, Habin ;
Kang, Byoungwoo .
SOLID STATE IONICS, 2014, 263 :125-130
[2]   Comparative study of lithium ion conductors in the system Li1-xAlxA2-xIV (PO4)3 with AIV = Ti or Ge and 0≤x≤0.7 for use as Li+ sensitive membranes [J].
Cretin, M ;
Fabry, P .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (16) :2931-2940
[3]   Challenges in the development of advanced Li-ion batteries: a review [J].
Etacheri, Vinodkumar ;
Marom, Rotem ;
Elazari, Ran ;
Salitra, Gregory ;
Aurbach, Doron .
ENERGY & ENVIRONMENTAL SCIENCE, 2011, 4 (09) :3243-3262
[4]   Lithium storage capability of lithium ion conductor Li1.5Al0.5Ge1.5(PO4)3 [J].
Feng, J. K. ;
Lu, L. ;
Lai, M. O. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 501 (02) :255-258
[5]   Solid-Electrolyte Interphase Formation and Electrolyte Reduction at Li-Ion Battery Graphite Anodes: Insights from First-Principles Molecular Dynamics [J].
Ganesh, P. ;
Kent, P. R. C. ;
Jiang, De-en .
JOURNAL OF PHYSICAL CHEMISTRY C, 2012, 116 (46) :24476-24481
[6]   The Li-Ion Rechargeable Battery: A Perspective [J].
Goodenough, John B. ;
Park, Kyu-Sung .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2013, 135 (04) :1167-1176
[7]  
Han XG, 2017, NAT MATER, V16, P572, DOI [10.1038/nmat4821, 10.1038/NMAT4821]
[8]   Degradation of NASICON-Type Materials in Contact with Lithium Metal: Formation of Mixed Conducting Interphases (MCI) on Solid Electrolytes [J].
Hartmann, Pascal ;
Leichtweiss, Thomas ;
Busche, Martin R. ;
Schneider, Meike ;
Reich, Marisa ;
Sann, Joachim ;
Adelhelm, Philipp ;
Janek, Juergen .
JOURNAL OF PHYSICAL CHEMISTRY C, 2013, 117 (41) :21064-21074
[9]  
Kamaya N, 2011, NAT MATER, V10, P682, DOI [10.1038/NMAT3066, 10.1038/nmat3066]
[10]   Integrated study of first principles calculations and experimental measurements for Li-ionic conductivity in Al-doped solid-state LiGe2(PO4)3 electrolyte [J].
Kang, Joonhee ;
Chung, Habin ;
Doh, Chilhoon ;
Kang, Byoungwoo ;
Han, Byungchan .
JOURNAL OF POWER SOURCES, 2015, 293 :11-16