Thermal properties of Al-Si/Al2O3 core-shell particles prepared by using steam hydration method

被引:24
作者
Han, Cangjuan [1 ]
Gu, Huazhi [1 ]
Zhang, Meijie [1 ]
Huang, Ao [1 ]
Zhang, Yi [1 ]
Wang, Yao [1 ]
机构
[1] Wuhan Univ Sci & Technol, State Key Lab Refractories & Met, Wuhan, Peoples R China
基金
中国国家自然科学基金;
关键词
Core-shell structure; Al-Si alloy; Latent heat storage; Latent heat release; Thermal property; PHASE-CHANGE MATERIALS; ENERGY STORAGE; SILICA SHELL; OXIDE-FILM; ACCELERATED-GROWTH; ALLOY CHEMISTRY; ALUMINUM-ALLOYS; VAPOR-PRESSURE; HEAT-CAPACITY; MOLTEN-SALT;
D O I
10.1016/j.jallcom.2019.152801
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this study, Al-Si/Al2O3 core-shell structured particles with a high heat storage were fabricated by keeping Al-Si alloy powder in pressurized steam for 0.5 h followed by heating at 900 degrees C and 1100 degrees C for 3 h, respectively. Both the melting and solidification point of termination for Al-Si/Al(2)O(3 )core-shell structured particles were delayed if the heating and cooling rate were too fast. The effect of heating and cooling rate on the latent heat was not obvious. Al-Si/Al2O3 core-shell structured particles prepared at 900 degrees C possessed relatively uniform shell and high latent heat, 292.0 Jg(-1), 74.8% of that of raw material. Even after 300 thermal cycles, the heat storage and heat release of this particles were still approximately 90% and 81% of that of particles before thermal cycling, while that of particles prepared at 1100 degrees C were 81.3% and 61.3%, respectively. The particles prepared at 900 degrees C has potential to be used as heat storage material or as raw material to fabricate heat storage ceramic such as ceramic honeycombs, ceramic heat storage balls and checker bricks, etc. (C) 2019 Elsevier B.V. All rights reserved.
引用
收藏
页数:9
相关论文
共 60 条
[31]   Nanoencapsulation of n-alkanes with poly(styrene-co-ethylacrylate) shells for thermal energy storage [J].
Konuklu, Yeliz ;
Paksoy, Halime O. ;
Unal, Murat .
APPLIED ENERGY, 2015, 150 :335-340
[32]   A review on phase change materials integrated in building walls [J].
Kuznik, Frederic ;
David, Damien ;
Johannes, Kevyn ;
Roux, Jean-Jacques .
RENEWABLE & SUSTAINABLE ENERGY REVIEWS, 2011, 15 (01) :379-391
[33]   Tunable endothermic plateau for enhancing thermal energy storage obtained using binary metal alloy particles [J].
Lai, Chih-Chung ;
Lin, Shih-Ming ;
Chu, Yuan-Da ;
Chang, Chun-Che ;
Chueh, Yu-Lun ;
Lu, Ming-Chang .
NANO ENERGY, 2016, 25 :218-224
[34]   Fabrication and Properties of Microencapsulated Paraffin@SiO2 Phase Change Composite for Thermal Energy Storage [J].
Li, Benxia ;
Liu, Tongxuan ;
Hu, Luyang ;
Wang, Yanfen ;
Gao, Lina .
ACS SUSTAINABLE CHEMISTRY & ENGINEERING, 2013, 1 (03) :374-380
[35]   Preparation and characterization of sodium thiosulfate pentahydrate/silica microencapsulated phase change material for thermal energy storage [J].
Liu, Chenzhen ;
Wang, Cui ;
Li, Yimin ;
Rao, Zhonghao .
RSC ADVANCES, 2017, 7 (12) :7238-7249
[36]   Review on storage materials and thermal performance enhancement techniques for high temperature phase change thermal storage systems [J].
Liu, Ming ;
Saman, Wasim ;
Bruno, Frank .
RENEWABLE & SUSTAINABLE ENERGY REVIEWS, 2012, 16 (04) :2118-2132
[37]   A review on current status and challenges of inorganic phase change materials for thermal energy storage systems [J].
Mohamed, Shamseldin A. ;
Al-Sulaiman, Fahad A. ;
Ibrahim, Nasiru I. ;
Zahir, Md Hasan ;
Al-Ahmed, Amir ;
Saidur, R. ;
Yilbas, B. S. ;
Sahin, A. Z. .
RENEWABLE & SUSTAINABLE ENERGY REVIEWS, 2017, 70 :1072-1089
[38]   Microencapsulation of eutectic and hyper-eutectic Al-Si alloy as phase change materials for high-temperature thermal energy storage [J].
Nomura, Takahiro ;
Yoolerd, Julalak ;
Sheng, Nan ;
Sakai, Hiroki ;
Hasegawa, Yuta ;
Haga, Miki ;
Saito, Genki ;
Akiyama, Tomohiro .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2018, 187 :255-262
[39]   Microencapsulated phase change materials with high heat capacity and high cyclic durability for high-temperature thermal energy storage and transportation [J].
Nomura, Takahiro ;
Sheng, Nan ;
Zhu, Chunyu ;
Saito, Genki ;
Hanzaki, Daiki ;
Hiraki, Takehito ;
Akiyama, Tomohiro .
APPLIED ENERGY, 2017, 188 :9-18
[40]   Microencapsulation of Metal-based Phase Change Material for High-temperature Thermal Energy Storage [J].
Nomura, Takahiro ;
Zhu, Chunyu ;
Sheng, Nan ;
Saito, Genki ;
Akiyama, Tomohiro .
SCIENTIFIC REPORTS, 2015, 5