The fatigue damage development in a cast Al-Si-Cu alloy

被引：32

作者：

Dietrich, Lech ^{[1
]}

Radziejewska, Joanna ^{[1
]}

机构：

[1] Polish Acad Sci, Inst Fundamental Technol Res, Dept Strength Mat, PL-02106 Warsaw, Poland

来源：

MATERIALS & DESIGN | 2011年 / 32卷 / 01期

关键词：

Cast aluminum alloy; Fatigue test; Fatigue damage; LIFE; BEHAVIOR; FRACTURE; VARIABILITY; STRENGTH; POROSITY; DEFECTS; CRACKS;

D O I：

10.1016/j.matdes.2010.05.045

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The experimental identification of fatigue damage mechanisms and evaluation of their development rate, based on changes in material respond on cycle loading, has been presented in the work. The research has been conducted on hyper-eutectic cast alloy AlSi8Cu3. The microstructure and fracture analyses were performed. The high cycle fatigue tests were conducted with frequency of 20 Hz under constant nominal stress amplitude with monitoring the strain response of material during the test. The ratcheting was found as the main mechanism of the fatigue damage. It was established that the linear fatigue accumulation law should not be used for fatigue life prediction in case of the tested cast aluminum alloy. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：322 / 329

页数：8

共 22 条

[1] Porosity and the fatigue behavior of hypoeutectic and hypereutectic aluminum-silicon casting alloys [J].

Ammar, H. R. ;

Samuel, A. M. ;

Samuel, F. H. .

INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (06) :1024-1035

[2] Effect of casting imperfections on the fatigue life of 319-F and A356-T6 Al-Si casting alloys [J].

Ammar, H. R. ;

Samuel, A. M. ;

Samuel, F. H. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 473 (1-2) :65-75

[3]

ANZELLOTTI G, 2009, 26 S ADV EXP MECH MO, P3

[4] Casting defects and fatigue strength of a die cast aluminium alloy: a comparison between standard specimens and production components [J].

Avalle, M ;

Belingardi, G ;

Cavatorta, MP ;

Doglione, R .

INTERNATIONAL JOURNAL OF FATIGUE, 2002, 24 (01) :1-9

[5] Low cycle fatigue life estimation for ductile metals using a nonlinear continuum damage mechanics model [J].

Bonora, N ;

Newaz, GM .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1998, 35 (16) :1881-1894

[6] Fatigue variability in Al-Si cast alloys [J].

Casellas, D ;

Pérez, R ;

Prado, JM .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 398 (1-2) :171-179

[7] The influence of heat treatment and solidification time on the behavior of small-fatigue-cracks in a cast aluminum alloy [J].

Caton, MJ ;

Jones, JW ;

Allison, JE .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 314 (1-2) :81-85

[8] Cumulative fatigue damage and life prediction theories: a survey of the state of the art for homogeneous materials [J].

Fatemi, A ;

Yang, L .

INTERNATIONAL JOURNAL OF FATIGUE, 1998, 20 (01) :9-34

[9] The role of defects in the fracture of an Al-Si-Mg cast alloy [J].

Francis, JA ;

Cantin, GMD .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 407 (1-2) :322-329

[10] The debonding and fracture of Si particles during the fatigue of a cast Al-Si alloy [J].

Gall, K ;

Yang, N ;

Horstemeyer, M ;

McDowell, DL ;

Fan, JH .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (12) :3079-3088

← 1 2 3 →