Synthesis and photoluminescence properties of a cyan-emitting phosphor Ca3(PO4)2:Eu2+ for white light-emitting diodes

In this paper, a cyan-emitting phosphor Ca-3(PO4)2:Eu2+ (TCP:Eu2+) was synthesized and evaluated as a candidate for white light emitting diodes (WLEDs). This phosphor shows strong and broad absorption in 250-450 nm region, but the emission spectrum is prominent at around 480 nm. The emission intensity of the TCP:Eu2+ was found to be 60% and 82% of that of the commercial BaMgAl10O17:Eu2+ (BAM) under excitation at 340 nm and 370 nm, respectively. Upon excitation at 370 nm, the absolute internal and external quantum efficiencies of the Ca-3(PO4)(2):1.5%Eu2+ are 60% and 42%, respectively. Moreover, a white LED lamp was fabricated by coating TCP:Eu2+ with a blue-emitting BAM and a red-emitting CaAlsiN(3):Eu2+ on a near-ultraviolet (375 nm) LED chip, driven by a 350 mA forward bias current, and it produces an intense white light with a color rendering index of 75. (C) 2014 Elsevier B.V. All rights reserved.