Hot deformation characterization of ultrahigh strength stainless steel through processing maps generated using different instability criteria

被引:44
|
作者
Wang, Xiaohui [1 ,2 ]
Liu, Zhenbao [2 ]
Luo, Haiwen [1 ]
机构
[1] Univ Sci & Technol Beijing, Sch Met & Ecol Engn, 30 Xue Yuan Lu, Beijing 100083, Peoples R China
[2] Cent Iron & Steel Res Inst, Div Special Steels, 76 Xue Yuan Nan Lu, Beijing 100081, Peoples R China
基金
中国国家自然科学基金; 对外科技合作项目(国际科技项目);
关键词
Ultrahigh strength; Stainless steel; Processing map; Hot deformation; Instability criterion; DYNAMIC RECRYSTALLIZATION; BEHAVIOR; ALLOY; MICROSTRUCTURE; SUPERALLOY; TEMPERATURE; WORKING;
D O I
10.1016/j.matchar.2017.07.041
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In order to avoid the unstable flow stress during the hot working of a newly designed ultrahigh strength stainless steel (UHSSS), we have constructed processing maps from the measured flow curves during hot compression over the wide ranges of temperature and strain rate using different instability/stability criteria. First, we developed power dissipation maps, in which we found some dynamic recrystallization (DRX) dominant regions characterized by low / values, leading to an exaggeration of the unstable flow region. Next, four types of processing maps were constructed according to the Murry and Rao (M-R), Kumar and Prasad (K-1) instability criteria, Gegel, Alexander and Malas (A-M) stability criteria respectively. After a critical evaluation on the difference in these criteria, we have proved that the Gegel and A-M instability criteria are mathematically equivalent and thus predict the same unstable region. The K-P and M-R criteria are equivalent only when the flow stress follows the exponential dependence of strain rate, i.e. alpha = K epsilon(m); The K-P instability and the A-M stabile criteria are same when - (m(2) + m(3)) < partial derivative m/partial derivative ln epsilon < 0 or they are just opposite when it is out of this range. Finally, we have concluded that the M-R criterion is capable of making prediction closest to the measured unstable region, which covers the deformation temperature range of 950-1080 degrees C and the strain rate range of 0.1-10 s(-1). The K-P criterion may overestimate the unstable flow region for the studied steel because the complicated interaction of dynamic precipitation and DRX that occurs during hot compression leads to a significant deviation of flow stress from the assumed exponential dependence on strain rate.
引用
收藏
页码:480 / 491
页数:12
相关论文
共 50 条
  • [1] Hot deformation behavior and processing maps of AISI 420 martensitic stainless steel
    Ren, Facai
    Chen, Fei
    Chen, Jun
    Tang, Xiaoying
    JOURNAL OF MANUFACTURING PROCESSES, 2018, 31 : 640 - 649
  • [2] Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps
    Momeni, A.
    Dehghani, K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (21-22): : 5467 - 5473
  • [3] Research on hot deformation characterization of a new weathering steel through processing map and microstructural observation
    Cheng, Jian
    SCIENTIFIC REPORTS, 2025, 15 (01):
  • [4] An Investigation into Hot Deformation Characteristics and Processing Maps of High-Strength Armor Steel
    Bobbili, Ravindranadh
    Madhu, V.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (12) : 4728 - 4735
  • [5] Development and Validation of Processing Maps for Hot Deformation of Modified AISI 321 Austenitic Stainless Steel
    Anoop, C. R.
    Singh, R. K.
    Kumar, Ravi Ranjan
    Miyala, Jayalakshmi
    Murty, S. V. S. Narayana
    Tharian, K. Thomas
    MATERIALS PERFORMANCE AND CHARACTERIZATION, 2020, 9 (02) : 150 - 169
  • [6] Hot Deformation and Processing Maps of a High Strength Alloy Steel
    Lin, Y. C.
    Liu, Ge
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 374 - 377
  • [7] Characterization of hot deformation behavior of wear-resistant steel BTW1 using processing maps and constitutive equations
    Liu, Peng-tao
    Huang, Qing-xue
    Ma, Li-feng
    Wang, Tao
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2018, 25 (10) : 1054 - 1061
  • [8] Hot deformation characterization of duplex low-density steel through 3D processing map development
    Mohamadizadeh, A.
    Zarei-Hanzaki, A.
    Abedi, H. R.
    Mehtonen, S.
    Porter, D.
    MATERIALS CHARACTERIZATION, 2015, 107 : 293 - 301
  • [9] Study on hot workability and optimization of process parameters of a modified 310 austenitic stainless steel using processing maps
    Sun, Hongying
    Sun, Yongduo
    Zhang, Ruiqian
    Wang, Man
    Tang, Rui
    Zhou, Zhangjian
    MATERIALS & DESIGN, 2015, 67 : 165 - 172
  • [10] Determining Hot Deformation Behavior of an Advance High Strength Steel (AHSS) by Means of Dynamic Processing Maps
    Gao, Xiang
    Ruvalcaba, Demian
    Han, Lu
    Li, HongXiang
    Santillana, Begona
    Zhuang, LinZhong
    ISIJ INTERNATIONAL, 2019, 59 (01) : 176 - 185