Effect of temperature on tensile behavior of Ni-Cr-W based superalloy

被引：96
作者：
Bai, Guanghai [1 ]
Li, Jinshan [1 ]
Hu, Rui [1 ]
Tang, Zengwu [1 ]
Xue, Xiangyi [1 ]
Fu, Hengzhi [1 ]
机构：
[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Peoples R China
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2011年 / 528卷 / 4-5期
关键词：
Ni-Cr-W based superalloy; Yield strength anomaly; M23C6; carbides; Tensile deformation; DEPENDENCE; CREEP; STRENGTH; CARBIDES; STRESS;
D O I：
10.1016/j.msea.2010.11.053
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The temperature dependence of tensile behavior of Ni-Cr-W based superalloy has been studied by tensile tests in the temperature range of 25-900 degrees C. The results indicated that the yield strength was anomaly with increasing temperature. Below 600 degrees C, both the tensile and yield strength decreased slightly with increasing temperature; above 600 degrees C, the tensile strength decreased rapidly while the yield strength almost kept invariable; the elongation had its minimum value at 600 degrees C. Microstructure analysis showed that M23C6 carbides including of lamellar carbides (600 degrees C) and discrete carbides (above 600 degrees C) precipitated at the grain boundaries. The lamellar M23C6 carbides with the width of 1-3 mu m weakened the strength of grain boundary, and thus led to the premature failure of the alloy. But the grain boundary sliding was effectively restricted by discrete M23C6 carbides. TEM analysis showed that the high dislocation density and cross-slip also contributed to the yield strength anomalous. (C) 2010 Elsevier B.V. All rights reserved.
引用
收藏
页码：1974 / 1978
页数：5
相关论文
共 20 条
[11]   INFLUENCE OF INTERGRANULAR CARBIDE DENSITY AND GRAIN-SIZE ON CREEP OF FE-15CR-25NI ALLOYS [J].
LI, PE ;
ZHANG, JS ;
WANG, FG ;
JIN, JZ .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (04) :1379-1381
[12]   Temperature dependence of tensile behavior of Ni-based superalloy M951 [J].
Lian, Z. W. ;
Yu, J. J. ;
Sun, X. F. ;
Guan, H. R. ;
Hu, Z. Q. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 489 (1-2) :227-233
[13]   Formation of carbides and their effects on stress rupture of a Ni-base single crystal superalloy [J].
Liu, LR ;
Jin, T ;
Zhao, NR ;
Sun, XF ;
Guan, HR ;
Hu, ZQ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 361 (1-2) :191-197
[14]   Hot working characteristic of as-cast and homogenized Ni-Cr-W superalloy [J].
Liu, Yi ;
Hu, Rui ;
Li, Jinshan ;
Kou, Hongchao ;
Li, Hongwei ;
Chang, Hui ;
Fu, Hengzhi .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 508 (1-2) :141-147
[15]   The dislocation microstructure of a nickel-base single-crystal superalloy after tensile fracture [J].
Luo, ZP ;
Wu, ZT ;
Miller, DJ .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 354 (1-2) :358-368
[16]   Mechanism of yield strength anomaly of Alloy 617 [J].
Roy, A. K. ;
Marthandam, V. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 517 (1-2) :276-280
[17]   Tensile deformation mechanisms at different temperatures in the Ni-base superalloy GTD-111 [J].
Sajjadi, SA ;
Nategh, S ;
Isac, M ;
Zebarjad, SM .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 155 :1900-1904
[18]   Formation and stability of nano-scaled M23C6 carbide in a directionally solidified Ni-base superalloy [J].
Wang, D. ;
Zhang, J. ;
Lou, L. H. .
MATERIALS CHARACTERIZATION, 2009, 60 (12) :1517-1521
[19]   Tensile deformation behavior of superalloy 718 at elevated temperatures [J].
Wang, Y. ;
Shao, W. Z. ;
Zhen, L. ;
Yang, C. ;
Zhang, X. M. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 471 (1-2) :331-335
[20]  
Watanabe Rikizo, 1977, United States Patent, Patent No. 4006015
12