Effect of temperature on tensile behavior of Ni-Cr-W based superalloy

被引：96

作者：

Bai, Guanghai ^{[1
]}

Li, Jinshan ^{[1
]}

Hu, Rui ^{[1
]}

Tang, Zengwu ^{[1
]}

Xue, Xiangyi ^{[1
]}

Fu, Hengzhi ^{[1
]}

机构：

[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2011年 / 528卷 / 4-5期

关键词：

Ni-Cr-W based superalloy; Yield strength anomaly; M23C6; carbides; Tensile deformation; DEPENDENCE; CREEP; STRENGTH; CARBIDES; STRESS;

D O I：

10.1016/j.msea.2010.11.053

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The temperature dependence of tensile behavior of Ni-Cr-W based superalloy has been studied by tensile tests in the temperature range of 25-900 degrees C. The results indicated that the yield strength was anomaly with increasing temperature. Below 600 degrees C, both the tensile and yield strength decreased slightly with increasing temperature; above 600 degrees C, the tensile strength decreased rapidly while the yield strength almost kept invariable; the elongation had its minimum value at 600 degrees C. Microstructure analysis showed that M23C6 carbides including of lamellar carbides (600 degrees C) and discrete carbides (above 600 degrees C) precipitated at the grain boundaries. The lamellar M23C6 carbides with the width of 1-3 mu m weakened the strength of grain boundary, and thus led to the premature failure of the alloy. But the grain boundary sliding was effectively restricted by discrete M23C6 carbides. TEM analysis showed that the high dislocation density and cross-slip also contributed to the yield strength anomalous. (C) 2010 Elsevier B.V. All rights reserved.

引用

页码：1974 / 1978

页数：5

共 20 条

[1]

[Anonymous], HAYN ON LIN LIT H 30

[2]

BEARDMORE P, 1969, T METALL SOC AIME, V245, P1537

[3] TEMPERATURE AND ORIENTATION DEPENDENCE OF YIELDING IN MAR-M200 SINGLE-CRYSTALS [J].

COPLEY, SM ;

ROWE, GM ;

KEAR, BH .

MATERIALS SCIENCE AND ENGINEERING, 1972, 10 (02) :87-&

[4] Effect of carbides on the creep properties of a Ni-base superalloy M963 [J].

He, LZ ;

Zheng, Q ;

Sun, XF ;

Guan, HR ;

Hu, ZQ ;

Tieu, AK ;

Lu, C ;

Zhu, HT .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 397 (1-2) :297-304

[5] Effects of heat treatment on microstructures and mechanical properties of a directionally solidified cobalt-base superalloy [J].

Jiang, WH ;

Guan, HR ;

Hu, ZQ .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 271 (1-2) :101-108

[6] Secondary carbide precipitation in a directionally solidified cobalt-base superalloy [J].

Jiang, WH ;

Yao, XD ;

Guan, HR ;

Hu, ZQ .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (03) :513-520

[7]

Kharitonova L. D., 1959, MET SCI HEAT TREAT, V1, P60

[8] ASSESSMENT OF SERVICE INDUCED MICROSTRUCTURAL DAMAGE AND ITS REJUVENATION IN TURBINE-BLADES [J].

KOUL, AK ;

CASTILLO, R .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1988, 19 (08) :2049-2066

[9] A NOTE ON THE MICROSTRUCTURAL DEPENDENCE OF CREEP STRENGTH IN INCONEL 700 [J].

KOUL, AK ;

WALLACE, W .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (04) :673-675

[10] CARBIDE MORPHOLOGY IN P-M IN-792 [J].

LARSON, JM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (10) :1497-1502

← 1 2 →