Investigation of Temperature Effects on Cavitation Erosion Behavior Based on Analysis of Erosion Particles

被引：14
作者：
Saleh, B. [1 ]
Abouel-Kasem, A. [1 ]
El-Deen, A. Ezz [1 ]
Ahmed, S. M. [1 ]
机构：
[1] Assiut Univ, Dept Mech Engn, Assiut 71516, Egypt
来源：
JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME | 2010年 / 132卷 / 04期
关键词：
cavitation erosion; temperature; erosion particles; characterization of particles; erosion mechanism; Al-99.92; ULTRASONIC CAVITATION; TESTS; PRESSURE; FAILURE; DAMAGE; STEEL;
D O I：
10.1115/1.4002069
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The effect of temperature on the wear particles produced by vibratory cavitation erosion tests on Al-99.92 in distilled water was analyzed. Scanning electron microscope images of wear particles were obtained, forming a database for further analysis. This study showed that the variation of average particle size with temperature was very much similar to the variation of weight loss with temperature. The average particle size was maximum at 40 degrees C. It was also observed that the average particle size was time dependent. The particle's morphology features revealed that the predominant erosion mechanism was fatigue failure, irrespective of the temperature. [DOI: 10.1115/1.4002069]
引用
收藏
页数：6
相关论文
共 50 条
  • [41] Comparative study on the cavitation erosion behavior of two different rolling surfaces on 304 stainless steel
    Li, Z. X.
    Zhang, L. M.
    Ma, A. L.
    Hu, J. X.
    Zhang, S.
    Daniel, E. F.
    Zheng, Y. G.
    TRIBOLOGY INTERNATIONAL, 2021, 159
  • [42] Investigation of Erosion/Corrosion Behavior of GRP under Harsh Operating Conditions
    Hassan, Mohamed K. K.
    Redhwi, Ahmad Muhammad N.
    Mohamed, Ahmed F. F.
    Backar, Ahmed N. H.
    Abdellah, Mohammed Y. Y.
    POLYMERS, 2022, 14 (24)
  • [43] Effects of microstructure and mechanical properties on cavitation erosion resistance of NiCrWMoCuCBFe coatings
    Wang, Yijing
    Hao, Enkang
    An, Yulong
    Chen, Jianmin
    Zhou, Huidi
    APPLIED SURFACE SCIENCE, 2021, 547
  • [44] Microstructure and cavitation erosion behavior of sputtered NiCrAlTi coatings with and without N incorporations
    Liu, Zhengliang
    Zhu, Shenglong
    Shen, Mingli
    Jia, Yixuan
    Wang, Wen
    Wang, Fuhui
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2020, 54 : 211 - 222
  • [45] Investigation of Erosion and Deposition Due to Flows with Particles
    Mehammer, Sol Johanne
    Greve, Martin M.
    Kosinski, Pawel
    Kosinska, Anna
    LANGMUIR, 2024, 40 (47) : 25154 - 25165
  • [46] COMPARATIVE INVESTIGATION OF ULTRASONIC CAVITATION EROSION FOR TWO ENGINEERING MATERIALS
    Volkov-Husovic, T.
    Martinovic, S.
    Alil, A.
    Vlahovic, M.
    Dimitrijevic, B.
    Ivanic, I.
    Pavkov, V.
    JOURNAL OF MINING AND METALLURGY SECTION B-METALLURGY, 2024, 60 (02) : 295 - 304
  • [47] In-situ study on cavitation erosion behavior of super ferritic stainless steel
    Wang, Zhenhua
    Zhang, Bing
    WEAR, 2021, 482
  • [48] Cavitation erosion behavior of Hastelloy™ C-276 weld by laser welding
    Chai, Dongsheng
    Ma, Guangyi
    Zhou, Siyu
    Jin, Zhuji
    Wu, Dongjiang
    WEAR, 2019, 420 : 226 - 234
  • [49] Effect of Surface Material on the Cavitation Erosion Noise: Experimental Investigation
    Ge Han
    Chen Haosheng
    Chen Darong
    Yan Dayun
    ADVANCED TRIBOLOGY, 2009, : 977 - 979
  • [50] Effect of temperature on cavitation erosion of 9Cr steel in liquid metal
    Hattori, Shuji
    Nimura, Akihiro
    Yada, Hiroki
    WEAR, 2013, 303 (1-2) : 269 - 275
12345