Mechanical properties of Al2O3-doped (2 wt.%) ZnO films

被引：12

作者：

Kuriki, Shina ^{[1
]}

Kawashima, Toshitaka ^{[1
]}

机构：

[1] Sony Corp, Core Component Business Unit, Core Technol Dev Grp, Shinagawa Ku, Tokyo 1410001, Japan

来源：

THIN SOLID FILMS | 2007年 / 515卷 / 24期

关键词：

transparent conductive oxide; ZnO : Al; mechanical properties; nano indentation; adhesion;

D O I：

10.1016/j.tsf.2007.04.005

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

We report a new method of evaluating the adhesion of Al2O3-doped (2 wt.%) ZnO (AZO) thin films. The AZO films were deposited by DC reactive magnetron sputtering on plastic film (PET: polyethylencterephthalatc) at various sputtering pressures, power, and reactive gas-flow ratios. The adhesion test of the films was carried out using the nanoindentation system. The fracture point as determined by the load-displacement curve occurred at the time of separation between the thin film and the substrate. The integration value of load and displacement to the fracture point is defined as the degree of adhesion (S-w). The AZO films showed that adhesion increase as sputtering power increases and sputtering pressure decreases. (c) 2007 Elsevier B.V. All rights reserved.

引用

页码：8594 / 8597

页数：4

共 10 条

[1] Properties of ZnO:Al films on polyester produced by de magnetron reactive sputtering [J].

Chen, M ;

Pei, ZL ;

Wang, X ;

Sun, C ;

Wen, LS .

MATERIALS LETTERS, 2001, 48 (3-4) :137-143

[2] INFLUENCE OF DISCHARGE PARAMETERS ON THE LAYER PROPERTIES OF REACTIVE MAGNETRON-SPUTTERED ZNO-AL FILMS [J].

ELLMER, K ;

KUDELLA, F ;

MIENTUS, R ;

SCHIECK, R ;

FIECHTER, S .

THIN SOLID FILMS, 1994, 247 (01) :15-23

[3] Review of analysis and interpretation of nanoindentation test data [J].

Fischer-Cripps, AC .

SURFACE & COATINGS TECHNOLOGY, 2006, 200 (14-15) :4153-4165

[4] Evaluation of PVD nitride coatings, using impact, scratch and Rockwell-C adhesion tests [J].

Heinke, W ;

Leyland, A ;

Matthews, A ;

Berg, G ;

Friedrich, C ;

Broszeit, E .

THIN SOLID FILMS, 1995, 270 (1-2) :431-438

[5]

LATZ R, 1991, JPN J APPL PHYS, V30, P149

[6] MEASUREMENT OF ADHERENCE OF RESIDUALLY STRESSED THIN-FILMS BY INDENTATION .1. MECHANICS OF INTERFACE DELAMINATION [J].

MARSHALL, DB ;

EVANS, AG .

JOURNAL OF APPLIED PHYSICS, 1984, 56 (10) :2632-2638

[7]

Minami T., 1984, JPN J APPL PHYS, V23, P280

[8] 'Pop-in' phenomenon during nanoindentation in epitaxial GaN thin films on c-plane sapphire substrates [J].

Navamathavan, R. ;

Moon, Yong-Tae ;

Kim, Gwang-Seok ;

Lee, Tae Geol ;

Hahn, Jun-Hee ;

Park, Seong-Ju .

MATERIALS CHEMISTRY AND PHYSICS, 2006, 99 (2-3) :410-413

[9] Measurement of the adhesion strength of metal oxide and metal nitride thin films sputtered onto glass by the direct pull-off method [J].

Suzuki, S ;

Hayashi, Y ;

Suzuki, K ;

Ando, E .

JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 1997, 11 (08) :1137-1147

[10] Fracture toughness, adhesion and mechanical properties of low-K dielectric thin films measured by nanoindentation [J].

Volinsky, AA ;

Vella, JB ;

Gerberich, WW .

THIN SOLID FILMS, 2003, 429 (1-2) :201-210

← 1 →