EFFECTS OF CRYSTAL ORIENTATION ON STRESS RUPTURE BEHAVIOR OF A Ni3Al-BASE SINGLE CRYSTAL SUPERALLOY IC6SX

The effect of the crystal orientation on the stress rupture behavior of the Ni3Al-base Single Crystal alloy IC6SX under the test condition of 1100 degrees C/120Mpa has been studied. The results showed that the stress rupture lives of the specimens with [001], [011] and [111] crystal orientations were 205.45h, 268.6h and 485h, respectively, i.e., the specimen with [111] crystal orientation had the longest stress rupture life. The results of the tests also showed the significant different of high temperature stress rupture elongation and area reduction for different crystal orientation specimens, i.e., the ruptured elongations for the specimens with [001], [011] and [111] crystal orientations were 61.9%, 22.9% and 28.8%, and the values of area reduction for the specimens with [001], [011] and [111] crystal orientations were 11.7%, 12.2% and 7.3% respectively.